- Clariant Renol PC010-L FR Polycarbonate, Glass Reinforced, Flame Retardant
Clariant Renol PC010-L FR Polycarbonate, Glass Reinforced, Flame Retardant
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol PC010-L FR Polycarbonate, Glass Reinforced, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 68.9 MPa | 10000 psi | ASTM D638 |
| Flexural Yield Strength | 103 MPa | 15000 psi | ASTM D790 |
| Flexural Modulus | 3.10 GPa | 450 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm @Temperature 22.8 °C |
1.30 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | 1/32, 1/16, 1/8, 1/4 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 271 - 293 °C | 520 - 560 °F | |
| Mold Temperature | 79.4 - 107 °C | 175 - 225 °F | |
| Dry Time | 2 - 4 hour @Temperature 121 °C |
2 - 4 hour @Temperature 250 °F |
to ensure moisture content is less than 0.02% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- Nye Lubricants 230 (SO) Synthetic Oil
- Abatron 4838 A/B Filled Potting Compound (discontinued **)
- Parker Chomerics CHO-BOND 1011, Part B
- Chevron Phillips 5497 LDPE High Clarity, Bakery Packaging Film Resin (discontinued **)
- Teknor Apex Sinvicomp SRP 5602 Polyvinyl Chloride, Rigid
- ChevronTexaco Clarity® ISO 100 Synthetic Paper Machine Oil
- BASF Ultramid® A3Z PA66 (Dry)
- Chang Chun Plastic PBT3030 30% Glass Fiber Enforced PBT
- Cheng Yu Plastic FV30G10 POM, 10% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved