Total PPH 6088 Polypropylene Homopolymer, Cast Film

Category Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Total Atofina
Trade Name PPH
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total PPH 6088 Polypropylene Homopolymer, Cast Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polypropylene PPH 6088 is a homopolymer polypropylene with a Melt Flow index of 9 g/10 min for the cast extrusion of film with excellent optical properties and good sterilizability.Polypropylene PPH 6088 is formulated with slip and anti-block agents. It is recommended for food packaging, textile packaging, flowers packaging, lamination films, and stationary supplies.Information provided by Total Petrochemicals.
Physical Properties Metric English Comments
Specific Gravity 0.905 g/cc
0.905 g/cc
ISO 1183
Bulk Density 0.525 g/cc
0.0190 lb/in³
ISO 1183
Thickness 50.0 microns
1.97 mil
Melt Flow 9.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
9.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Antiblock Level 1800 ppm
1800 ppm
SiO2
Slip Level 1800 ppm
1800 ppm
Erucamide
Mechanical Properties Metric English Comments
Hardness, Rockwell R 95
95
ISO 2039-2
Film Tensile Strength at Yield, MD 22.0 MPa
3190 psi
ISO 527-3
Film Tensile Strength at Yield, TD 22.0 MPa
3190 psi
ISO 527-3
Tensile Strength, Yield 30.0 MPa
4350 psi
ISO 527-2
Film Elongation at Break, MD 700 %
700 %
ISO 527-3
Film Elongation at Break, TD 700 %
700 %
ISO 527-3
Elongation at Yield 10 %
10 %
ISO 527-2
Tensile Modulus 1.40 GPa
203 ksi
ISO 527-2
Flexural Modulus 1.30 GPa
189 ksi
ISO 178
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
ISO 180
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
ISO 179
Elmendorf Tear Strength, MD 1.40 g/micron
35.6 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 2.80 g/micron
71.1 g/mil
ISO 6383-2
Dart Drop Test 280 g
0.617 lb
ISO 7765-1
Film Tensile Strength at Break, MD 60.0 MPa
8700 psi
ISO 527-3
Film Tensile Strength at Break, TD 55.0 MPa
7980 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 160 °C
320 °F
ISO 3146
Deflection Temperature at 0.46 MPa (66 psi) 100 °C
212 °F
120°C per hour; ISO 752
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
120°C per hour; ISO 752
Vicat Softening Point 87.0 °C

@Load 5.10 kg
189 °F

@Load 11.2 lb
50°C per hour; ISO 306
152 °C

@Load 1.02 kg
306 °F

@Load 2.25 lb
50°C per hour; ISO 306
Optical Properties Metric English Comments
Haze 1.4 %
1.4 %
ISO 14782
Gloss 89 %
89 %
at 45°; ASTM D2457