Clariant Renol PA11BK FDA Nylon 66, General Purpose, FDA, Black
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol PA11BK FDA Nylon 66, General Purpose, FDA, Black.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.017 cm/cm | 0.017 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 82.7 MPa | 12000 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Flexural Yield Strength | 138 MPa | 20000 psi | ASTM D790 |
| Flexural Modulus | 2.83 GPa | 410 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm @Temperature 22.8 °C |
1.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C | 171 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 271 - 293 °C | 520 - 560 °F | |
| Mold Temperature | 65.6 - 79.4 °C | 150 - 175 °F | |
| Dry Time | 2 - 4 hour @Temperature 71.1 °C |
2 - 4 hour @Temperature 160 °F |
to eliminate surface defects |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- RheTech Products T20P100-01 20% Talc Reinforced Polypropylene, Black
- Qualchem Danamid AFES-23 Polyamide 66
- Kolon KOCETAL® K300LO Low Odor Acetal Resin
- Indium Corp. Indalloy 114 Tin-Lead Solder Alloy
- Seals Eastern 7352D Nano-PTFE Filled Fluoroelastomer
- Covestro Makroblend® S 7916/2 Polycarbonate + PBT, Impact Grade
- Daikin NEOFLON AF-2400 PFA Film
- Axiall 11441 Wire & Cable Flexible PVC
- BASF Ultramid® B3WG5 25% Glass Filled PA6 (Dry)
Copyright © lookpolymers.com All Rights Reserved