Clariant Renol CAB1000 Cellulose Acetate Butyrate
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Cellulosic , Cellulose Acetate Butyrate, Molded |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol CAB1000 Cellulose Acetate Butyrate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 43.4 MPa | 6300 psi | ASTM D638 |
| Elongation at Yield | 40 % | 40 % | ASTM D638 |
| Flexural Yield Strength | 49.0 MPa | 7100 psi | ASTM D790 |
| Flexural Modulus | 1.59 GPa | 230 ksi | ASTM D790 |
| Izod Impact, Notched | 2.14 J/cm @Temperature 22.8 °C |
4.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 77.2 °C | 171 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 188 - 232 °C | 370 - 450 °F | |
| Mold Temperature | 51.7 - 79.4 °C | 125 - 175 °F | |
| Dry Time | 2 - 4 hour @Temperature 71.1 - 82.2 °C |
2 - 4 hour @Temperature 160 - 180 °F |
|
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- Karina TR-500D10/1-YV White PVC Compound
- LyondellBasell Petrothene® NA940094 Low Density Polyethylene (Film Grade)
- ELASTO UK Dryflex® 8009-101 Flame Retardant TPE for Extrusion, Black
- DSM Akulon® K225-KWS (Cond.) Nylon 6 (North America)
- Fainplast Compounds GK 80/R Flexible PVC, Flame Retardant Sheathing Lead Free
- Fainplast Compounds GS 75/O Flexible PVC, Injection Molding for Footwear
- 3M 4496W Double Coated Polyethylene Foam Tape
- DSM Akulon® K225-KV PA6 FR(30)
Copyright © lookpolymers.com All Rights Reserved