A. Schulman FORMION™ FI 335 Ionomer
| Category | Polymer , Thermoplastic , Ionomer |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman FORMION™ FI 335 Ionomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ISO 1183/1 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0060 in/in @Thickness 0.126 in |
72 hr; ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 | 65 | 15 sec delay; ISO 868 |
| Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | at max load; ISO 527 |
| Elongation at Break | 22 % | 22 % | ISO 527 |
| Flexural Modulus | 0.685 GPa | 99.4 ksi | Tangent; ISO 178 |
| Izod Impact, Notched (ISO) | 28.0 kJ/m² | 13.3 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 44.0 °C @Thickness 3.20 mm |
111 °F @Thickness 0.126 in |
ISO 75 |
Users viewing this material also viewed the following:
- MV Labs LA400 LaCl3·7H2O Lanthanum chloride heptahydrate
- Oxford Polymers C-Acetal 10MF-900 BK Acetal
- SABIC Innovative Plastics Lexan® 241R PC
- LATI Laticonther 80 CPG/700 PPS, Glass Fiber Reinforced
- A. Schulman SCHULADUR® A GF20HI 20% Glass Fiber Reinforced, High Impact PBT
- ChevronTexaco Syn-Star® GL SAE 75W-90
- Dow DOWLEX™ 2077G Linear Low Density Polyethylene
Copyright © lookpolymers.com All Rights Reserved