DSM Akulon® Ultraflow K-FPG8 PA6-I-GF40
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Akulon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Akulon® Ultraflow K-FPG8 PA6-I-GF40.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Glass Reinforced, High flow
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | dry; ISO 1183 |
| Water Absorption | 5.7 % | 5.7 % | Sim. To ISO 62 |
| Moisture Absorption | 1.70 % | 1.70 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0036 cm/cm | 0.0036 in/in | ISO 204-4 |
| Linear Mold Shrinkage, Transverse | 0.0089 cm/cm | 0.0089 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | cond; ISO 527-1/-2 |
| 175 MPa | 25400 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 3.5 % | 3.5 % | dry; ISO 527-1/-2 |
| 7.0 % | 7.0 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 7.31 GPa | 1060 ksi | cond; ISO 527-1/-2 |
| 11.5 GPa | 1670 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | 8.99 J/cm² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU |
| 8.99 J/cm² @Temperature -30.0 °C |
42.8 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eU | |
| 9.49 J/cm² @Temperature -30.0 °C |
45.2 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eU | |
| 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU | |
| Charpy Impact, Notched | 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eA |
| 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eA | |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA | |
| 3.00 J/cm² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 65.0 µm/m-°C | 36.1 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | dry; ISO 75-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | cond; IEC 60093 |
| >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | dry; IEC 60093 | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | cond; IEC 60093 |
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz |
3.3 @Frequency 1.00e+6 Hz |
dry; IEC 60250 |
| 3.5 @Frequency 100 Hz |
3.5 @Frequency 100 Hz |
dry; IEC 60250 | |
| 4.5 @Frequency 1.00e+6 Hz |
4.5 @Frequency 1.00e+6 Hz |
cond; IEC 60250 | |
| 14 @Frequency 100 Hz |
14 @Frequency 100 Hz |
cond; IEC 60250 | |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | cond; IEC 60243-1 |
| 25.0 kV/mm | 635 kV/in | dry; IEC 60243-1 | |
| Dissipation Factor | 0.0090 @Frequency 100 Hz |
0.0090 @Frequency 100 Hz |
dry; IEC 60250 |
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
dry; IEC 60250 | |
| 0.12 @Frequency 1.00e+6 Hz |
0.12 @Frequency 1.00e+6 Hz |
cond; IEC 60250 | |
| 0.30 @Frequency 100 Hz |
0.30 @Frequency 100 Hz |
cond; IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | cond; IEC 60112 |
Users viewing this material also viewed the following:
- DuPont Performance Polymers Hypalon® 45 Chlorosulfonated Polyethylene Rubber, Uncured Carbon Black Filled Compound &
- IRPC Polimaxx Polene BM3245 PC High Density Polyethylene
- Mitsubishi Xantar® F 25 UR Polycarbonate
- SABIC Innovative Plastics LNP LUBRICOMP EX10404H PEI
- Spartech PP5110 Talc Filled Homopolymer
- SABIC Innovative Plastics LNP THERMOCOMP DF0069P PC
- A. Schulman POLYBATCH™ White P8555 T2 Concentrate Based In Homopolymer Polypropylene
- ConocoPhillips Synterra™ 1 Hydraulic Oil, AGMA No. 1
- PolyOne Edgetek® NI-30CF/000 Nylon 6/10 - 30% Carbon Fiber Reinforced (discontinued **)
- NOVA Chemicals Sclair® 11J4 Octene LLDPE Film Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved