SABIC Innovative Plastics LNP STAT-LOY 63000CTC PC+POLYESTER (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Stat-loy |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-LOY 63000CTC PC+POLYESTER (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A permanent antistatic PC-Alloy compound that features transparency and superior cleanliness for advanced semiconductor packaging applications
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.700 % | 0.700 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | 5 mm/min; ISO 527 |
| 35.0 MPa | 5080 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 140 % | 140 % | 5 mm/min; ISO 527 |
| 200 % | 200 % | Type I, 10 mm/min; SABIC - Japan Method | |
| Tensile Modulus | 1.17 GPa | 170 ksi | 50 mm/min; ASTM D638 |
| 1.19 GPa | 173 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 52.0 MPa | 7540 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 1.15 GPa | 167 ksi | 2 mm/min; ISO 178 |
| 1.17 GPa | 170 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 5.80 J/cm | 10.9 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 6.90 J/cm² | 32.8 ft-lb/in² | ISO 179/2C |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 120 µm/m-°C @Temperature 23.0 - 60.0 °C |
66.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 140 µm/m-°C @Temperature 23.0 - 60.0 °C |
77.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C @Thickness 6.40 mm |
183 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C @Thickness 6.40 mm |
167 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 25 % @Thickness 2.54 mm |
25 % @Thickness 0.100 in |
ASTM D1003 |
| Transmission, Visible | 77 % | 77 % | 2.54 mm; ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 8.00e+9 - 3.00e+11 ohm-cm | 8.00e+9 - 3.00e+11 ohm-cm | ASTM D257 |
| Surface Resistance | 9.00e+9 - 4.00e+11 ohm | 9.00e+9 - 4.00e+11 ohm | ASTM D257 |
| Static Decay | 2.0 sec | 2.0 sec | 5000V to <50V; FTMS101B |
Users viewing this material also viewed the following:
- Oxford Polymers PEI 30GF-Natural PEI, 30% Glass Fiber Reinforced
- SABIC Innovative Plastics Geloy CR7520 ASA (Europe-Africa-Middle East)
- Premix Thermoplastics PRE-ELEC® 12-032 (discontinued **)
- 3M Dyneon™ TF 5060 PTFE Dispersion (discontinued **)
- Samsung Cheil Industries Starex® TX-0510T TRABS, Unreinforced
- Saint-Gobain Chemfab® 13 Tear Resistant PTFE-Coated Glass
- Engineered Plastics EPPC 2014G Polycarbonate
- Braskem IJ33D LLDPE Injection Molding Polyethylene Copolymer
- 3M 477 Vinyl Tape
- Loctite® 415 General Purpose Methyl Cyanoacrylate Bonding Adhesive
Copyright © lookpolymers.com All Rights Reserved