Clariant Renol 612G20-L Nylon 612, 20% Glass Fiber Reinforced, Lubricated
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 , Nylon 612, Glass Fiber Filler |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol 612G20-L Nylon 612, 20% Glass Fiber Reinforced, Lubricated.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D790 |
| Filler Content | 20 % | 20 % | ASTM D2584 |
| Linear Mold Shrinkage | 0.0060 - 0.0070 cm/cm | 0.0060 - 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 103 MPa | 15000 psi | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 179 MPa | 26000 psi | ASTM D790 |
| Flexural Modulus | 5.17 GPa | 750 ksi | ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm @Temperature 22.8 °C |
1.10 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 208 °C | 406 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 189 °C | 372 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 243 - 271 °C | 470 - 520 °F | |
| Mold Temperature | 79.4 - 107 °C | 175 - 225 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C |
2 - 4 hour @Temperature 175 °F |
to ensure moisture level is less than 0.2% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.172 - 0.517 MPa | 25.0 - 75.0 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- Kingfa FRHIPS-960 Flame Retardant Polystyrene
- Shandong Dongyue Shenzhou New Material Co CHFM 175 Perfluorosulfonic Acid Proton Exchange Membrane (PFSAPEM)
- Spartech SP-3010 Rigid PVC Specialty Sheet
- Saint-Gobain Chemfab® 313X PTFE Coated Fiberglass Conveyor Belting
- SABIC Innovative Plastics LNP THERMOTUF IX02582 PA6.12
- Lubrizol ESTANE® 58277 Ester Based Thermoplastic Polyurethane (European Grade)
- Zotefoams Plastazote® LD15FMSV Low Density Polyethylene Foam, Flame Retarded
- DSM Novamid® 2420A PA666
- ATI Allegheny Ludlum AL 50™ High Strength Stainless Steel, UNS S20910
- Overview of materials for Nylon 6, 30% Glass Fiber Filled
Copyright © lookpolymers.com All Rights Reserved