DuPont Elvaloy® 1126 AC Ethylene and 25% Methyl Acrylate Copolymer (discontinued **)
| Category | Polymer , Film , Thermoplastic , Ethylene Methyl Acrylate , Ethylene-Methyl Acrylate Copolymer, Molding Grade |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Elvaloy® 1126 AC Ethylene and 25% Methyl Acrylate Copolymer
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Elvaloy® 1126 AC is intended for coextrusion and molding. It can be recommended for blow molding of parts requiring permanent flexibility, stress cracking resistance and softness. Excellent filler acceptance makes Elvaloy® 1126 AC suitable for highly filled compounds.Elvaloy® 1126 AC is easily processed on standard equipment used for low-density polyethylene.Information provided by DuPont.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.944 g/cc | 0.0341 lb/in³ | ASTM D792 - ISO 1183 |
| Melt Flow | 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.60 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 - ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 78 | 78 | ASTM D2240 - ISO 868 |
| Hardness, Shore D | 19 | 19 | ASTM D2240 - ISO 868 |
| Tensile Strength at Break | 14.0 MPa | 2030 psi | 500 mm/min; ASTM D638 - ISO 527-2 |
| Elongation at Break | 860 % | 860 % | 500 mm/min; ASTM D638 - ISO 527-2 |
| Tensile Modulus | 0.0190 GPa | 2.76 ksi | 1 mm/min; ASTM D638 - ISO 527-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 90.0 °C | 194 °F | By DSC; ASTM D3418 - ISO 3146 |
| Vicat Softening Point | 45.0 °C | 113 °F | A<sub>50</sub> (10N); ASTM D1525 - ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 140 - 160 °C | 284 - 320 °F | For blow molding |
| Rear Barrel Temperature | 150 °C | 302 °F | Extrusion lamination and extrusion coating |
| 150 °C | 302 °F | Cast film | |
| 150 °C | 302 °F | Blown film | |
| Middle Barrel Temperature | 160 °C | 320 °F | Blown film |
| 210 °C | 410 °F | Cast film | |
| 220 °C | 428 °F | Extrusion lamination | |
| Front Barrel Temperature | 170 °C | 338 °F | Blown film |
| 250 °C | 482 °F | Cast film | |
| 290 °C | 554 °F | Extrusion lamination | |
| Adapter Temperature | 180 °C | 356 °F | Blown film |
| 250 °C | 482 °F | Cast Film | |
| 290 °C | 554 °F | Extrusion lamination | |
| Die Temperature | 180 °C | 356 °F | Blown film |
| 250 °C | 482 °F | Cast film | |
| 290 °C | 554 °F | Extrusion lamination |
| Descriptive Properties | Value | Comments |
|---|---|---|
| MA-Content | 25 wt.% | DuPont Method |
Users viewing this material also viewed the following:
- Overview of materials for Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend
- Manifattura Cattaneo PE UMW Polyethylene
- Materion Beryllium Copper Alloy 10 Forgings & Extrusions; A (TB00) Temper (UNS C17500)
- Polyram PlusTek PB320G3 Nylon 6, 15% Glass Fiber, Flame Retardant
- DSM Stanyl® 46HF5040 Nylon 46-40% Glass Reinforced (European and Asian Grade) (Cond)
- BorsodChem ONGROSTYR F-I Expandable Polystyrene (EPS)
- Aptek 6513-A/B Versatile, fast set adhesive
- Permabond 792 Cyanoacrylate, Surface insensitive
Copyright © lookpolymers.com All Rights Reserved