- Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
- Chi Mei Polylac® PA-763A ABS - Flame Retardant
Chi Mei Polylac® PA-763A ABS - Flame Retardant
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Polylac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Polylac® PA-763A ABS - Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
F.R. High Heat
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1189 |
| Melt Flow | 28 g/10 min @Load 10.0 kg, Temperature 220 °C |
28 g/10 min @Load 22.0 lb, Temperature 428 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 80.0 MPa | 11600 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 33.0 MPa | 4790 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 20 % | 20 % | 50 mm/min; ISO 527 |
| Flexural Strength | 60.0 MPa | 8700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.10 GPa | 305 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 22.0 kJ/m² | 10.5 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180/1C |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 2.20 J/cm² | 10.5 ft-lb/in² | ISO 179 |
| Impact | 14.0 | 14.0 | Impact Flexural Test Notched (KJ/m²) |
| NB | NB | Impact Flexural Test Unnotched (KJ/m²) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | unannealed; ISO 75 |
| 97.0 °C | 207 °F | annealed; ISO 75 | |
| Vicat Softening Point | 97.0 °C @Load 5.00 kg |
207 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 98.0 °C @Load 5.00 kg |
208 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 104 °C @Load 1.00 kg |
219 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| 105 °C @Load 1.00 kg |
221 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | V-0 @Thickness 1.59 mm |
V-0 @Thickness 0.0625 in |
UL 94 |
| 5VB @Thickness 2.54 mm |
5VB @Thickness 0.100 in |
UL 94 |
Users viewing this material also viewed the following:
- Network Polymers SAN 290 Light Blue Tint
- Polyram PE322G22 PET, 22% Glass Fiber (discontinued **)
- Styron CALIBREâ„¢ 201-10 Polycarbonate Resin
- SABIC Innovative Plastics LNP VERTON MV006SU PP (Europe-Africa-Middle East)
- A. Schulman POLYBATCH™ Light Grey LL803366/4 Concentrate Based In LLDPE
- ELASTO UK Dryflex® 502500S SEBS Based Material, Unfilled Qualities, 50A Hardness, Black
- Buckeye Polymers BP ABS 3333 R BLK ABS Polymer
- 3M Controltac™ 162-10 Graphic Film
- PolyOne Edgetek® ATH-15GF/000 Acetal-Homopolymer, Glass Filled (discontinued **)
Copyright © lookpolymers.com All Rights Reserved