ExxonMobil LDPE LD 144BR Low Density Polyethylene Resin

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer	Exxon Chemical
Trade Name	LDPE
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil LDPE LD 144BR Low Density Polyethylene Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: LD 144BR is an LDPE grade, which offers excellent optical properties combined with increased stiffness and drawdown properties.Availability: Africa & Middle East and Europe Additive: Antiblock: 1000 ppmSlip: 750 ppmThermal Stabilizer: YesApplications: Blend PartnerBread BagsCast FilmCo-Extrusion FilmsDisplay Packaging FilmFood packagingForm Fill and Seal Packaging High Clarity FilmLaundry FilmLight Duty Shrink Film Mail BagOverwrap FilmProduce BagsSalad Bags Information provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	0.927 g/cc	0.0335 lb/in³	ExxonMobil method
Melt Flow	3.1 g/10 min @Load 2.16 kg, Temperature 190 °C	3.1 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Antiblock Level	1000 ppm	1000 ppm
Slip Level	750 ppm	750 ppm

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	13.1 MPa	1900 psi	ASTM D882
Film Tensile Strength at Yield, TD	11.7 MPa	1700 psi	ASTM D882
Film Elongation at Break, MD	190 %	190 %	ASTM D882
Film Elongation at Break, TD	470 %	470 %	ASTM D882
Elmendorf Tear Strength MD	250 g	250 g	ASTM D1922
Elmendorf Tear Strength TD	130 g	130 g	ASTM D1922
Dart Drop Test	60.0 g	0.132 lb	ASTM D1709A
Film Tensile Strength at Break, MD	22.1 MPa	3200 psi	ASTM D882
Film Tensile Strength at Break, TD	17.2 MPa	2500 psi	ASTM D882
1% Secant Modulus, MD	241 MPa	35000 psi	ASTM D882
1% Secant Modulus, TD	283 MPa	41000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	<= 234 °C	<= 453 °F	Peak Melting Point; ExxonMobil method

Optical Properties	Metric	English	Comments
Haze	5.5 %	5.5 %	ASTM D1003
Gloss	75 %	75 %	45°; ASTM D2457