Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
Manufacturer | CP-Polymer-Technik GmbH & Co. |
Trade Name | Wellamid® |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | CP-Polymer-Technik Wellamid® 6600 GV 25 DCHP 25% Glass Fiber Nylon 66, Special Heat Ageing Stabilization, Dry.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183 |
Moisture Absorption at Equilibrium | 2.0 - 2.5 % | 2.0 - 2.5 % | 23°C/50%RH; DIN 53495 |
Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 4.00 mm |
0.0020 in/in @Thickness 0.157 in |
|
Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Thickness 4.00 mm |
0.0070 in/in @Thickness 0.157 in |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 160 MPa | 23200 psi | 5 mm/min; ISO 527 |
Elongation at Break | 3.5 % | 3.5 % | 5 mm/min; ISO 527 |
Tensile Modulus | 8.20 GPa | 1190 ksi | ISO 527 |
Flexural Modulus | 7.40 GPa | 1070 ksi | DIN 52457 |
Charpy Impact Unnotched | 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
Charpy Impact, Notched | 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 30.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
16.7 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 53752 |
Melting Point | 255 °C | 491 °F | Kofler |
Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 179 |
Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 179 |
Vicat Softening Point | 230 °C | 446 °F | 50 N; ISO 306 |
Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
Stufe; IEC 707 |
HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
Stufe; IEC 707 |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | ISO 3915 |
Dielectric Constant | 4.0 @Frequency 1e+6 Hz |
4.0 @Frequency 1e+6 Hz |
IEC 250 |
Dielectric Strength | 40.0 kV/mm | 1020 kV/in | IEC 243-1 |
Dielectric Loss Index | 0.015 | 0.015 | At 1 MHz; IEC 250 |
Comparative Tracking Index | 550 V | 550 V | Stufe; IEC 112 |
Processing Properties | Metric | English | Comments |
---|---|---|---|
Melt Temperature | 265 - 295 °C | 509 - 563 °F | |
Mold Temperature | 70.0 - 100 °C | 158 - 212 °F |
Descriptive Properties | Value | Comments |
---|---|---|
Back Pressure | Low | |
Holding Pressure | High | |
Injection Speed | High | |
Screw Speed | Medium |