CP-Polymer-Technik Wellamid® 6000 S Nylon 6, Finely Crystalline, Conditioned

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer CP-Polymer-Technik GmbH & Co.
Trade Name Wellamid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF CP-Polymer-Technik Wellamid® 6000 S Nylon 6, Finely Crystalline, Conditioned.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by CP-Polymer-Technik GmbH & Co. KG
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 2.5 - 3.3 %
2.5 - 3.3 %
23°C/50%RH, Starting when dry; DIN 53495
Linear Mold Shrinkage 0.0080 - 0.012 cm/cm

@Thickness 4.00 mm
0.0080 - 0.012 in/in

@Thickness 0.157 in
Mechanical Properties Metric English Comments
Tensile Strength, Yield 50.0 MPa
7250 psi
50 mm/min; ISO 527
Elongation at Break >= 50 %
>= 50 %
50 mm/min; ISO 527
Elongation at Yield 15 %
15 %
50 mm/min; ISO 527
Tensile Modulus 1.10 GPa
160 ksi
ISO 527
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179
Charpy Impact, Notched 1.00 J/cm²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
Melting Point 215 °C
419 °F
Kofler
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
IEC 93
Surface Resistance 1.00e+10 ohm
1.00e+10 ohm
ISO 3915
Dielectric Constant 7.0

@Frequency 1e+6 Hz
7.0

@Frequency 1e+6 Hz
IEC 250
Dielectric Strength 35.0 kV/mm
889 kV/in
IEC 243-1
Dielectric Loss Index 0.30
0.30
At 1 MHz; IEC 250
Processing Properties Metric English Comments
Melt Temperature 245 - 265 °C
473 - 509 °F
Mold Temperature 40.0 - 80.0 °C
104 - 176 °F
Descriptive Properties Value Comments
Back Pressure Low
Holding Pressure High
Injection Speed Medium to High
Screw Speed High