- HOME
- POLYMER SEARCH
- Thermoplastic
- Nylon
- Nylon 6
- CP-Polymer-Technik Wellamid® 6000 MX 400 CP Combination Nylon 6, Heat Stabilized, Conditioned
CP-Polymer-Technik Wellamid® 6000 MX 400 CP Combination Nylon 6, Heat Stabilized, Conditioned
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | CP-Polymer-Technik GmbH & Co. |
| Trade Name | Wellamid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CP-Polymer-Technik Wellamid® 6000 MX 400 CP Combination Nylon 6, Heat Stabilized, Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by CP-Polymer-Technik GmbH & Co. KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.8 - 2.5 % | 1.8 - 2.5 % | 23°C/50%RH, Starting when dry; DIN 53495 |
| Linear Mold Shrinkage | 0.0050 cm/cm @Thickness 4.00 mm |
0.0050 in/in @Thickness 0.157 in |
|
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Thickness 4.00 mm |
0.0070 in/in @Thickness 0.157 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 10 % | 10 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 5.50 GPa | 798 ksi | ISO 527 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179 |
| Charpy Impact, Notched | 1.80 J/cm² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 215 °C | 419 °F | Kofler |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | ISO 3915 |
| Dielectric Constant | 6.0 @Frequency 1e+6 Hz |
6.0 @Frequency 1e+6 Hz |
IEC 250 |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 243-1 |
| Dielectric Loss Index | 0.10 | 0.10 | At 1 MHz; IEC 250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 290 °C | 482 - 554 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Holding Pressure | Medium | |
| Injection Speed | Medium to High | |
| Screw Speed | High |
Users viewing this material also viewed the following:
- Lanxess Durethan® BKV 35 H2.0 EF 900116 Nylon 6, 35% Glass Fiber
- SABIC Innovative Plastics Valox® 8032UX PBT+PET (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP THERMOCOMP DF0029P PC
- Borealis HJ325MO Polypropylene
- ChevronTexaco Gear Compounds EP, ISO 220
- Cytec Thornel® Mat VME Carbon Fiber
- Arlon 55572XA028 0.028" (0.711 mm) Cured Silicone Rubber with Fiberglass Substrate
- Chem Polymer Chemlon 218 GV Nylon 6, 18% Glass Reinforced
- Saint-Gobain CHR® 2045-10 Skived PTFE Film Backing Silicone Adhesive Pressure Sensitive Tape
Copyright © lookpolymers.com All Rights Reserved