- CP-Polymer-Technik Wellamid® 6000 GS 15 HWCP 15% Glass Sphere Filled Nylon 6, Heat Stabilized, Dry
CP-Polymer-Technik Wellamid® 6000 GS 15 HWCP 15% Glass Sphere Filled Nylon 6, Heat Stabilized, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Bead Filled |
| Manufacturer | CP-Polymer-Technik GmbH & Co. |
| Trade Name | Wellamid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CP-Polymer-Technik Wellamid® 6000 GS 15 HWCP 15% Glass Sphere Filled Nylon 6, Heat Stabilized, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by CP-Polymer-Technik GmbH & Co. KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.2 - 3.0 % | 2.2 - 3.0 % | 23°C/50%RH; DIN 53495 |
| Linear Mold Shrinkage | 0.0080 - 0.010 cm/cm @Thickness 4.00 mm |
0.0080 - 0.010 in/in @Thickness 0.157 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 9.0 % | 9.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 3.50 GPa | 508 ksi | ISO 527 |
| Flexural Modulus | 3.00 GPa | 435 ksi | DIN 52457 |
| Charpy Impact Unnotched | 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Charpy Impact, Notched | 0.500 J/cm² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 53752 |
| Melting Point | 215 °C | 419 °F | Kofler |
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ISO 179 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 179 |
| Vicat Softening Point | 200 °C | 392 °F | 50 N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
Stufe; IEC 707 |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
Stufe; IEC 707 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | ISO 3915 |
| Dielectric Constant | 4.0 @Frequency 1e+6 Hz |
4.0 @Frequency 1e+6 Hz |
IEC 250 |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 243-1 |
| Dielectric Loss Index | 0.020 | 0.020 | At 1 MHz; IEC 250 |
| Comparative Tracking Index | 450 V | 450 V | Stufe; IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Holding Pressure | High | |
| Injection Speed | Medium | |
| Screw Speed | High |
Users viewing this material also viewed the following:
- Nabaltec GRANALOX® NM 9634 F Ceramic Body
- Flint Hills P4C6S-193A Homopolymer Polypropylene
- Karina E 10/31-RG-GE White Color Concentrate for PVC
- Solvay Specialty Polymers AvaSpire® AV-722 CF30 Polyaryletherketone (PAEK), 30% Carbon Fiber
- Tipco Tipcolene® CR 6216 - 40% Talc/Mineral Reinforced Polypropylene Copolymer Compound with Controlled Rheology
- Eastman Tenite 371A2R30008 Cellulose Acetate Propionate, Natural, Trsp
- ExxonMobil 150 Mobil DTE PM Series
- Eurostar Starflam RF0023K PA66/6, Glass Fiber Filled, Flame Retardant, Injection Molded
- Clariant PA131 Nylon 66, Highly Impact Modified
- Akro-Plastic Akromid® B3 GF 20 (2470) PA 6 Conditioned, 20% Glass Filled
Copyright © lookpolymers.com All Rights Reserved