Beijing Chemical Industry KAIFA® MN201-G30 Nylon 66 Resin
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Beijing Chemical Industry Research Institute (Group) |
| Trade Name | KAIFA® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Beijing Chemical Industry KAIFA® MN201-G30 Nylon 66 Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% glass fiber reinforced, thermal resistantInformation provided by Beijing Chemical Industry Research Institute (Group)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 150 MPa | 21800 psi | ASTM D638 |
| Flexural Strength | 210 MPa | 30500 psi | ASTM D790 |
| Charpy Impact Unnotched | 7.50 J/cm² | 35.7 ft-lb/in² | ISO179 |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.1 @Frequency 1e+6 Hz |
3.1 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 30.0 kV/mm @Thickness 2.00 mm |
762 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dissipation Factor | 0.030 @Frequency 1e+6 Hz |
0.030 @Frequency 1e+6 Hz |
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |
| Middle Barrel Temperature | 265 - 270 °C | 509 - 518 °F | |
| Front Barrel Temperature | 265 - 270 °C | 509 - 518 °F | |
| Nozzle Temperature | 265 - 270 °C | 509 - 518 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 90.0 - 120 MPa | 13100 - 17400 psi |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® MC8100 PC+ABS (Asia Pacific)
- Northstar Polymers MPP-V37A Polyurethane Gel Elastomer
- SABIC Innovative Plastics SABIC PPCOMPOUND 19T1040 PP
- SABIC Innovative Plastics LNP STAT-LOY A3000 ABS (Europe-Africa-Middle East)
- DuPont Performance Polymers Crastin® SK642FR NC010 Polybutylene Terephthalate (PBT)
- Ascend Performance Materials Vydyne® R540 Nylon 66, 40% Glass Reinforced, Conditioned
- Axiall 8922 Moldings & Extrusions Flexible PVC
- Asahi Glass Fluon® LM-730AP LM-ETFE Fluororesin
- 3M Controltac™ 180 Graphic Film
- 3M Dyneon™ FC 2177D Fluoroelastomer
Copyright © lookpolymers.com All Rights Reserved