Azoty Tarnow™ TARNOFORM 500 GB6 POM

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Glass Bead Filled
Manufacturer Azoty Tarnow™ (Zaklady Azotowe)
Trade Name TARNOFORM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Azoty Tarnow™ TARNOFORM 500 GB6 POM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% glass beads filled low viscosity grade with very high stiffness and hardness with lowered shrinkage combined with easy molding of complicated shapesInformation provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.
Physical Properties Metric English Comments
Density 1.59 g/cc
0.0574 lb/in³
ISO 1183
Water Absorption 0.22 %
0.22 %
23°C/24 hr; ISO 62
Melt Flow 20 g/10 min

@Load 2.16 kg,
Temperature 190 °C
20 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 112
112
ISO 2039-2
Ball Indentation Hardness 202 MPa
29300 psi
358 N; ISO 2039-1
Tensile Strength, Yield 41.0 MPa
5950 psi
ISO 527
Elongation at Break 8.0 %
8.0 %
ISO 527
Flexural Strength 69.0 MPa
10000 psi
ISO 178
Izod Impact, Notched (ISO) 3.50 kJ/m²
1.67 ft-lb/in²
1A; ISO 180
Charpy Impact, Notched 0.200 J/cm²
0.952 ft-lb/in²
1eA; ISO 179
Thermal Properties Metric English Comments
Melting Point 167 °C
333 °F
10°C/min.; ISO 3146
Deflection Temperature at 1.8 MPa (264 psi) 129 °C
264 °F
ISO 75
Vicat Softening Point 150 °C
302 °F
50 N; ISO 306
Flammability, UL94 HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Dielectric Constant 4.4

@Frequency 1e+6 Hz
4.4

@Frequency 1e+6 Hz
IEC 60250
4.9

@Frequency 100 Hz
4.9

@Frequency 100 Hz
IEC 60250
Dielectric Strength 30.0 kV/mm
762 kV/in
IEC 60243
Dissipation Factor 0.0115

@Frequency 1e+6 Hz
0.0115

@Frequency 1e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 112
Processing Properties Metric English Comments
Processing Temperature 180 - 230 °C
356 - 446 °F
Barrel temperature
Mold Temperature 60.0 - 120 °C
140 - 248 °F