Karina E 105852-35/1-A-IS-L Ivory PVC Compound
| Category | Polymer , Thermoplastic , Vinyl (PVC) |
| Manufacturer | Karina Indústria e Comércio de Plásticos |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Karina E 105852-35/1-A-IS-L Ivory PVC Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PVC compound recommended for extrusion of wires THHN and THWN.Information provided by Karina Indústria e Comércio de Plásticos Ltda.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 - 1.37 g/cc | 1.31 - 1.37 g/cc | NBR NM-IEC 60811-1-3 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 83 - 87 @Time 15.0 sec |
83 - 87 @Time 0.00417 hour |
NBR 7456 |
| Tensile Strength | >= 13.8 MPa | >= 2010 psi | NBR NM-IEC 60811-1-1 |
| >= 13.8 MPa | >= 2010 psi | After 168 H in Air Oven at 136°C; NBR NM-IEC 60811-1-2 | |
| Elongation at Break | >= 150 % | >= 150 % | NBR NM-IEC 60811-1-1 |
| >= 150 % | >= 150 % | After 168H in Air Oven at 136°C; NBR NM-IEC 60811-1-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | NBR 5403 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Application | 105 Grades | |
| 80 Grades | ||
| Maximum Variation of Elongation (%) | 25 | NBR NM-IEC 60811-1-2 |
| Maximum Variation of Tensile Strength (%) | 25 | NBR NM-IEC 60811-1-2 |
Users viewing this material also viewed the following:
- Polymer Resources PC-FD3 Polycarbonate, FDA-compliant Feedstocks, High Flow, Gamma Resistant
- Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 5% cold reduction
- Kingfa PBT-G15 15% Glass Fiber Reinforced PBT
- Solvay Specialty Polymers Amodel® A-4122 NL WH 905 Polyphthalamide (PPA), 22% Glass Fiber
- Solvay TECHNYL® A 216 PA66, Conditioned
- A. Schulman POLYBATCH™ White P8555 T2 Concentrate Based In Homopolymer Polypropylene
- DSM Stanyl® TW371 (DAM) Nylon 46 Heat Stabilized, PTFE Lubricated (North America)
- A. Schulman ComAlloy Hiloy® 420 Polyester - PBT, Glass/Mineral Reinforced
- Permabond A126 Anaerobic Retainer
Copyright © lookpolymers.com All Rights Reserved