BASF Ultrason E 2010 G4 20% Glass Filled PES
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone (PES), 20%Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultrason E |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultrason E 2010 G4 20% Glass Filled PES.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultrason E 2010 G4 is a 20% glass reinforced, medium viscosity injection molding PES grade with high rigidity and strength.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 |
| Water Absorption | 1.6 % | 1.6 % | ISO 62 |
| Moisture Absorption at Equilibrium | 0.60 % | 0.60 % | 23°C/50% R.H.; ISO 62 |
| Viscosity Test | 56 cm³/g | 56 cm³/g | Viscosity number |
| Linear Mold Shrinkage, Flow | 0.0036 cm/cm | 0.0036 in/in | ISO Data |
| Linear Mold Shrinkage, Transverse | 0.0061 cm/cm | 0.0061 in/in | ISO Data |
| Melt Flow | 29 g/10 min @Load 10.0 kg, Temperature 360 °C |
29 g/10 min @Load 22.0 lb, Temperature 680 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 205 MPa | 29700 psi | ISO 2039-1 |
| Tensile Strength at Break | 125 MPa | 18100 psi | 5mm/min; ISO 527-2 |
| Tensile Strength, Yield | 125 MPa | 18100 psi | 50mm/min; ISO 527-2 |
| Elongation at Break | 2.5 % | 2.5 % | 5mm/min; ISO 527-2 |
| Elongation at Yield | 2.5 % | 2.5 % | 50mm/min; ISO 527-2 |
| Tensile Modulus | 7.30 GPa | 1060 ksi | Elasticity; ISO 527-2 |
| Shear Modulus | 0.200 GPa @Temperature 225 °C |
29.0 ksi @Temperature 437 °F |
ISO 6721 |
| 0.900 GPa @Temperature 200 °C |
131 ksi @Temperature 392 °F |
ISO 6721 | |
| 0.950 GPa @Temperature 100 °C |
138 ksi @Temperature 212 °F |
ISO 6721 | |
| 1.00 GPa @Temperature 50.0 °C |
145 ksi @Temperature 122 °F |
ISO 6721 | |
| Izod Impact, Notched (ISO) | 6.50 kJ/m² | 3.09 ft-lb/in² | ISO 180/A |
| 6.50 kJ/m² @Temperature -30.0 °C |
3.09 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A | |
| Charpy Impact Unnotched | 4.70 J/cm² | 22.4 ft-lb/in² | ISO 179/1eU |
| 4.50 J/cm² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.650 J/cm² | 3.09 ft-lb/in² | ISO 179/1eA |
| 0.650 J/cm² @Temperature -30.0 °C |
3.09 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |
| Tensile Creep Modulus, 1000 hours | 5600 MPa | 812000 psi | ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
11.1 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 |
| 23.0 µm/m-°C @Temperature 140 - 180 °C |
12.8 µin/in-°F @Temperature 284 - 356 °F |
ISO 180/A | |
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | DIN 52612-1 |
| Maximum Service Temperature, Air | 220 °C | 428 °F | |
| 220 °C | 428 °F | short cycle operations | |
| Deflection Temperature at 0.46 MPa (66 psi) | 224 °C | 435 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75-2 |
| Glass Transition Temp, Tg | 225 °C | 437 °F | ISO 11357-1/-3 |
| UL RTI, Electrical | 180 °C | 356 °F | 50% decrease of tensile strength after 20000h; 746B |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
||
| Oxygen Index | 44.5 % | 44.5 % | ISO 4589-1/-2 |
| Glow Wire Test | 825 °C | 1520 °F | Ignition Temperature; IEC 60695-2-13 |
| 960 °C | 1760 °F | Flammability Index; IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 4.2 @Frequency 100 Hz |
4.2 @Frequency 100 Hz |
IEC 60250 |
| 4.2 @Frequency 1.00e+6 Hz |
4.2 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Dielectric Strength | 37.0 kV/mm | 940 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0020 @Frequency 100 Hz |
0.0020 @Frequency 100 Hz |
IEC 60250 |
| 0.010 @Frequency 1.00e+6 Hz |
0.010 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 125 V | 125 V | Test Liquid A & B; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 350 - 390 °C | 662 - 734 °F | Injection molding |
| Mold Temperature | 150 - 190 °C | 302 - 374 °F | Injection molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | North America and Europe | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® OQ4620 PC
- Plansee DENAL® 920 60 20 Tungsten-Nickel-Iron-Cobalt Alloy
- Polymer Resources NY6-IM1-[color]-H Nylon 6, Impact Modified, Heat Stabilized
- PolyOne Edgetek® AS-1000 Acrylonitrile Butadiene Styrene (ABS) (discontinued **)
- Lehmann & Voss LUVOCOM® 21-8113 Polyamide 6/6T, with carbon fiber, lubricant modified
- Lehmann & Voss LUVOCOM® 80-7653 Polyacetal-copolymer, with carbon fiber
- Spartech 3030-10005 PVC and Alloy Products for Wire and Cable
- Suqian Unitechem Antioxidant 626
- Ensinger XP-151 Compression Molded PI Compound, 15% Graphite Filled, Premium Grade
- SABIC Innovative Plastics LNP Thermocomp PF007 PA 6 (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved