Kingfa JH960 6610 Non-halogenated Flame Retardant PC/ABS Alloy

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Kingfa Sci. & Tech. Co.
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kingfa JH960 6610 Non-halogenated Flame Retardant PC/ABS Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features:Halogen free flame retardant, V-0/1.5mmExcellent balance propertiesHigh heat resistanceGood chemical resistanceGood hydrolysis resistanceSuit for paint and electo-platingDrop down resistanceApplications:LCD TV, monitor, PDPLaser printer, photocopierNotebook computer and chargerRechargeable cellAutomobile DVDPower tool and chargerTelecommunication equipmentInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc

@Temperature 23.0 °C
 1.20 g/cc

@Temperature 73.4 °F
 ASTM D792
Water Absorption 0.12 %

@Temperature 23.0 °C,
Time 86400 sec
 0.12 %

@Temperature 73.4 °F,
Time 24.0 hour
 ASTM D570
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm

@Temperature 23.0 °C
 0.0040 - 0.0060 in/in

@Temperature 73.4 °F
 ASTM D955
Melt Flow 19 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 19 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ASTM D785
Tensile Strength at Break 65.0 MPa
9430 psi
50mm/min; ASTM D638
Elongation at Break 50 %
50 %
50mm/min; ASTM D638
Flexural Strength 100 MPa
14500 psi
2mm/min; ASTM D790
Flexural Modulus 3.70 GPa
537 ksi
2mm/min; ASTM D790
Izod Impact, Notched 3.80 J/cm

@Thickness 3.20 mm,
Temperature -10.0 °C
 7.12 ft-lb/in

@Thickness 0.126 in,
Temperature 14.0 °F
 ASTM D256
8.00 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 15.0 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 127 °C

@Thickness 6.40 mm
 261 °F

@Thickness 0.252 in
 ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 115 °C

@Thickness 6.40 mm
 239 °F

@Thickness 0.252 in
 ASTM D648
Flammability, UL94 5VB

@Thickness 1.60 mm
 5VB

@Thickness 0.0630 in
5VA

@Thickness 3.20 mm
 5VA

@Thickness 0.126 in
Electrical Properties Metric English Comments
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
ASTM D257
Dielectric Strength 19.0 kV/mm
483 kV/in
1.6mm; ASTM D149
Processing Properties Metric English Comments
Processing Temperature <= 265 °C
<= 509 °F
Rear Barrel Temperature 230 - 255 °C
446 - 491 °F
Start Point: 235°C
Middle Barrel Temperature 230 - 260 °C
446 - 500 °F
Start Point: 245°C
Front Barrel Temperature 235 - 270 °C
455 - 518 °F
Start Point: 255°C
Melt Temperature 230 - 260 °C
446 - 500 °F
Start Point: 240°C
Mold Temperature 40.0 - 80.0 °C
104 - 176 °F
Start Point: 60°C
Drying Temperature 80.0 - 90.0 °C

@Time 7200 - 14400 sec
 176 - 194 °F

@Time 2.00 - 4.00 hour
 Pre-dry
Back Pressure 0.300 - 0.700 MPa
43.5 - 102 psi
Descriptive Properties Value Comments
Injection Speed 50-80%