Samsung Cheil Industries Starex® CR-0760 ABS, Unreinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® CR-0760 ABS, Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Good chemical resistanceInformation provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Melt Flow | 3.7 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.7 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 106 | 106 | ASTM D785 |
| Tensile Strength, Yield | 41.2 MPa | 5970 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 57.9 MPa | 8400 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.77 J/cm @Thickness 6.35 mm |
3.31 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 95.0 °C | 203 °F | B/50; ISO R306 |
Users viewing this material also viewed the following:
- Kazanorgsintez 293-285SK High Density Polyethylene Composite, Film Grade
- Kolon KOPA® KN133G30 G/F Reinforced Nylon 6
- Shin-Etsu Silicones X-22-6711B Fluid
- Westlake Hifor LT74105 Linear Low Density Polyethylene
- A. Schulman PP 828-01 Polypropylene Molding Grade Impact Polypropylene
- Eagle Brass 151 ZHC® COPPER, Hard
- 3M 33803 General Purpose Aluminum Foil Tape
- ExxonMobil Escorene® LD-724 High EVA Compounding Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved