ExxonMobil LL 8360 Rotational Molding Resin (discontinued **)

Category	Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Rotational Molding Grade
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil LL 8360 Rotational Molding Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LL 8360 is a linear low density hexene copolymer designed to provide good processability along with outstanding dimensional control and low warpage. This resin is ideally suited for applications that require excellent processability and ESCR along with optimum balance of stiffness and low temperature toughness.Information provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.932 g/cc	0.0337 lb/in³	ASTM D4883
ESCR 100% Igepal®	>= 1000 hour	>= 1000 hour	ASTM D1693
ESCR 10% Igepal®	650 hour	650 hour	ASTM D1693
Melt Flow	5.2 g/10 min	5.2 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	15.2 MPa	2200 psi	ASTM D638
Elongation at Yield	20.6 %	20.6 %	ASTM D638
Flexural Modulus	0.600 GPa	87.0 ksi	1% secant; ASTM D790
Impact Test	88.1 J @Thickness 3.17 mm, Temperature -40.0 °C	65.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F	ARM
	217 J @Thickness 6.35 mm, Temperature -40.0 °C	160 ft-lb @Thickness 0.250 in, Temperature -40.0 °F	ARM

Thermal Properties	Metric	English	Comments
Melting Point	125 °C	257 °F	ASTM D3418
Crystallization Temperature	111.2 °C	232.2 °F	ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi)	55.0 °C	131 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	37.0 °C	98.6 °F	ASTM D648