BASF Ultramid® A3X2G7 35% Glass Filled PA66 (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant
Manufacturer	BASF
Trade Name	Ultramid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® A3X2G7 35% Glass Filled PA66 (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ultramid A3X2G7 is a 35% glass fiber reinforced injection molding PA66 grade with improved flame retardance and enhanced long-term stability. Flame retardant based on red phosphorus; very high stiffness and strength; outstanding mechanical and electrical properties.

Physical Properties	Metric	English	Comments
Density	1.45 g/cc	0.0524 lb/in³	ISO 1183
Water Absorption	4.4 - 5.0 %	4.4 - 5.0 %	ISO 62
Moisture Absorption at Equilibrium	1.0 - 1.4 %	1.0 - 1.4 %	(23°C/50% R.H.); ISO 62
Viscosity Test	140 cm³/g	140 cm³/g	Viscosity number; ISO 307
Linear Mold Shrinkage	0.0045 cm/cm	0.0045 in/in
Melt Flow	43.5 g/10 min @Load 5.00 kg, Temperature 275 °C	43.5 g/10 min @Load 11.0 lb, Temperature 527 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	120 MPa	17400 psi	50mm/min; ISO 527
Elongation at Yield	4.0 %	4.0 %	50mm/min; ISO 527
Modulus of Elasticity	8.50 GPa	1230 ksi	ISO 527
Izod Impact, Notched (ISO)	20.0 kJ/m²	9.52 ft-lb/in²	ISO 180/A
Charpy Impact Unnotched	7.00 J/cm²	33.3 ft-lb/in²	ISO 179/1eU
Charpy Impact, Notched	1.80 J/cm²	8.57 ft-lb/in²	ISO 179/1eA
Tensile Creep Modulus, 1000 hours	4250 MPa	616000 psi	ISO 899-1

Thermal Properties	Metric	English	Comments
Specific Heat Capacity	1.40 J/g-°C	0.335 BTU/lb-°F
Thermal Conductivity	0.340 W/m-K	2.36 BTU-in/hr-ft²-°F	DIN 52612
Melting Point	260 °C	500 °F	Test Solution A; DIN 53765
Maximum Service Temperature, Air	140 °C	284 °F	for 50% loss of tensile strength after 20,000 hr
	157 °C	315 °F	for 50% loss of tensile strength after 5,000 hr
	220 °C	428 °F

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+10 ohm-cm	1.00e+10 ohm-cm	IEC 60093
Surface Resistance	1.00e+10 ohm	1.00e+10 ohm	IEC 60093
Dielectric Constant	5.0 @Frequency 1.00e+6 Hz	5.0 @Frequency 1.00e+6 Hz	IEC 60250
Dissipation Factor	0.20 @Frequency 1.00e+6 Hz	0.20 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	IEC 60112

Processing Properties	Metric	English	Comments
Melt Temperature	280 - 300 °C	536 - 572 °F	Injection-molding/Extrusion
Mold Temperature	80.0 - 90.0 °C	176 - 194 °F	Injection-molding

Descriptive Properties	Value	Comments
Color	Natural
Commercial Status	Active America
Form	Pellets
Impact Modified	No
Primary Processing Technique	Injection Molding
Processing	Injection Molding
Special characteristic	Flame retarding agent
	Heat stabilized or stable to heat
	Release agent