Network Polymers MS 110 Styrene Methyl Methacrylate Terpolymer
| Category | Polymer , Thermoplastic , Acrylic (PMMA) , Polystyrene (PS) , Styrene/Methyl Methacrylate Copolymer (SMMA) |
| Manufacturer | Network Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Network Polymers MS 110 Styrene Methyl Methacrylate Terpolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Styrene Methyl Methacrylate TerpolymerInformation provided by Network Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 0.40 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.40 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 64.1 MPa | 9300 psi | chs 2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | chs 2 in/min; ASTM D638 |
| Tensile Modulus | 3.45 GPa | 500 ksi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 3.02 GPa | 438 ksi | Test Method I, Procedure B (chs speed 0.05 in/min); ASTM D790 |
| Izod Impact, Notched | 0.246 J/cm | 0.460 ft-lb/in | 0.125 inch bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | ASTM D648 |
| Vicat Softening Point | 101 °C | 214 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 89 % | 89 % | ASTM D1003 |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPC TS20020 UV Polypropylene Copolymer, Mineral Reinforced, UV-Stabilized
- ExxonMobil Santoprene® 8291-85PA Thermoplastic Elastomer (discontinued **)
- Mid-Mountain Materials SILTEX® XS-150 Silica Yarn
- Kuraray Genestarâ„¢ G1352A-M41 Nylon, 35% Glass Filled
- Techmer ES Elastoblend® PA6/6 GF43 IM L 43% Glass Filled
- Loctite® 420 General Purpose Ethyl Cyanoacrylate Bonding Adhesive
- Eurotec® Tecomid® NA40 KC50 BK111 PA6.6, 50% glass/carbon fiber reinforced, black
- Carlson 20 Plus Alloy
- Alliance Polymers Viprene™ G65A-32U-BLK Thermoplastic Vulcanizate Elastomer
- Arkema Group OREVAC® 9307 Y EVA Terpolymer
Copyright © lookpolymers.com All Rights Reserved