Polymer Property : Modulus of Elasticity = 1.10 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	1.10 GPa	160 ksi
Murtfeldt Muralen® Black Antistatic Polyethylene, Conductive Muralen® is based on high molecular weight polyethylene (PE-HMW) and is ideally suited for use in applications that require the generally impressive material properties of polyethylene. Because of..
Modulus of Elasticity	1.10 GPa	160 ksi
Murtfeldt Muralen® plus + AB Polyethylene, Antibacterial Muralen® is based on high molecular weight polyethylene (PE-HMW) and is ideally suited for use in applications that require the generally impressive material properties of polyethylene. Because of..
Modulus of Elasticity	1.10 GPa	160 ksi
Murtfeldt Muralen® Polyethylene Muralen® is based on high molecular weight polyethylene (PE-HMW) and is ideally suited for use in applications that require the generally impressive material properties of polyethylene. Because of..
Modulus of Elasticity	1.10 GPa @Thickness 4.00 mm	160 ksi @Thickness 0.157 in	10.0 mm wide molded rod; ISO 178
Premix Thermoplastics PRE-ELEC® PE 1292 PRE-ELEC PE 1292 is a conductive thermoplastic compound based on PE-HD. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC PE 129..
Modulus of Elasticity	1.10 - 1.70 GPa	160 - 247 ksi	ASTM D638-04
Proto3000 Objet Digital Materials™ DM_8430 Polypropylene-like Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide..
Modulus of Elasticity	1.10 - 1.70 GPa	160 - 247 ksi	ASTM D638-04
Proto3000 Objet Digital Materials™ DM_8530_Gray60 Polypropylene-like Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoBlackPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to pr..
Modulus of Elasticity	1.10 - 17.0 GPa @Temperature 60.0 - 175 °C	160 - 2470 ksi @Temperature 140 - 347 °F	Average value: 10.4 GPa Grade Count:5
Overview of materials for Polyphthalamide (PPA), 50% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 50% Glass Fiber Reinforced". Each property range of values reported is minimum and maxi..
Modulus of Elasticity	1.10 - 2.69 GPa	160 - 390 ksi	Average value: 1.93 GPa Grade Count:16
Overview of materials for PETG Copolyester This property data is a summary of similar materials in the MatWeb database for the category "PETG Copolyester". Each property range of values reported is minimum and maximum values of appropriate M..
Modulus of Elasticity	1.10 - 5.60 GPa	160 - 812 ksi	Average value: 2.03 GPa Grade Count:253
Overview of materials for Polystyrene, Impact Modified This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene, Impact Modified". Each property range of values reported is minimum and maximum values of a..
Modulus of Elasticity	1.10 - 2.40 GPa	160 - 348 ksi	Average value: 1.78 GPa Grade Count:4
Overview of materials for Polypropylene, Mineral Reinforced, Impact Modified This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Mineral Reinforced, Impact Modified". Each property range of values reported is minimum a..
Modulus of Elasticity	1.10 - 3.45 GPa	160 - 500 ksi	Average value: 2.19 GPa Grade Count:85
Overview of materials for Polypropylene with 20% Talc Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 20% Talc Filler".Specific grades with primary filler content between 15% and 24% are ..
Modulus of Elasticity	1.10 - 12.4 GPa	160 - 1800 ksi	Average value: 3.02 GPa Grade Count:64
Overview of materials for Nylon 66, Unreinforced, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Unreinforced, Flame Retardant". Each property range of values reported is minimum and maximum ..
Modulus of Elasticity	1.10 - 28.0 GPa	160 - 4060 ksi	Average value: 7.84 GPa Grade Count:105
Overview of materials for Nylon 66, Heat Stabilized This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Heat Stabilized". Each property range of values reported is minimum and maximum values of appr..
Modulus of Elasticity	1.10 GPa @Temperature 20.0 Â°C	160 ksi @Temperature 68.0 Â°F
Micropol Isoplas P381 Crosslinkable Polyethylene Information provided by Micropol Limited
Modulus of Elasticity	1.10 GPa	160 ksi	ISO 527-1/-2
BASF Ultramid® C3U10 BK 23079 PA6/66 FR (Conditioned) Description: Flame-retardant injection-molding grade; light colorable. Burning behavior optimized for glow-wire requirements of IEC 60335. Typical applications are switches, housings, plug connector..
Modulus of Elasticity	1.10 GPa	160 ksi	ISO 527-1/-2
BASF Ultramid® C3U10 PA6/66 FR (Conditioned) Description: Flame-retardant injection-molding grade; light colorable. Burning behavior optimized for glow-wire requirements of IEC 60335. Typical applications are switches, housings, plug connector..
Modulus of Elasticity	1.10 GPa	160 ksi	ISO 527-1/-2
BASF Ultramid® S3K Balance PA 610 (Conditioned) Description: BASF supplies polyamide 610 for processing by injection molding under the trade name Ultramid® Balance which is produced by polycondensation of hexamethylene diamine and sebacic acid. ..
Modulus of Elasticity	1.10 GPa	160 ksi	ISO 527-1/-2
BASF Ultramid® A3K BK 00464 PA66 (Conditioned) Description: Easy flowing injection-molding grade for fast processing. Uses include highly stressed technical parts such as bearings and gear wheels; also electrically insulating parts such as termi..
Modulus of Elasticity	1.10 GPa	160 ksi	ISO 527-1/-2
BASF Ultramid® A3W PA66 (Conditioned) Description: Free-flowing, heat aging resistant and rapidly processable grade for technical parts subject to high stress such as bearings and bearing cages, gearwheels and spool bodies.Information p..
Modulus of Elasticity	1.10 GPa	160 ksi	1 mm/min; ASTM D638
Solvay Specialty Polymers Solef® 11008 PVDF Copolymer (discontinued **) Key features of this grade: Low Viscosity, Wire & Cable, Plenum, Formulated. Recommended processing is extrusion. Available as powder & granules.General information about SOLEF® PVDF: SOLEF® PVD..
Modulus of Elasticity	1.10 - 1.90 GPa	160 - 276 ksi	Average value: 1.64 GPa Grade Count:9
Overview of materials for Polypropylene with 10% Mica Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 10% Mica Filler". Specific grades with primary filler content between 5% and 14% are ..