BASF Ultramid® A3EG3 15% Glass Filled PA66 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® A3EG3 15% Glass Filled PA66 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid A3EG3 is a 15% glass fiber reinforced injection molding PA66 grade. It conforms to FDA requirements of 21 CFR 177.1500.
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
ISO 1183
Water Absorption 7.0 %
7.0 %
ISO 62
Moisture Absorption at Equilibrium 2.2 %
2.2 %
23°C/50% R.H.; ISO 62
Viscosity Test 145 cm³/g
145 cm³/g
Viscosity number
Linear Mold Shrinkage 0.0055 cm/cm
0.0055 in/in
ASTM Data; MD
Melt Flow 70 g/10 min

@Load 5.00 kg,
Temperature 275 °C
70 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 114 MPa
16500 psi
0.2 in/min; ASTM Test
156 MPa

@Temperature -40.0 °C
22600 psi

@Temperature -40.0 °F
ISO Data
Tensile Strength, Ultimate 130 MPa
18900 psi
5mm/min; ISO 527
Tensile Strength, Yield 74.0 MPa

@Temperature 80.0 °C
10700 psi

@Temperature 176 °F
ISO Data
Elongation at Break 3.0 %
3.0 %
5mm/min; ISO 527
3.0 %
3.0 %
0.2 in/min; ASTM Test
2.6 %

@Temperature -40.0 °C
2.6 %

@Temperature -40.0 °F
ISO Data
Elongation at Yield 7.4 %

@Temperature 80.0 °C
7.4 %

@Temperature 176 °F
ISO Data
Tensile Modulus 5.86 GPa
850 ksi
ASTM Test
6.00 GPa
870 ksi
1mm/min; ISO 527
Flexural Strength 180 MPa
26100 psi
ISO Data
Flexural Modulus 5.17 GPa
750 ksi
ASTM Test
5.20 GPa
754 ksi
ISO Data
Izod Impact, Notched 0.530 J/cm

@Temperature -40.0 °C
0.993 ft-lb/in

@Temperature -40.0 °F
ASTM Test
0.590 J/cm

@Thickness 3.17 mm
1.11 ft-lb/in

@Thickness 0.125 in
ASTM Test
Izod Impact, Notched (ISO) 5.50 kJ/m²
2.62 ft-lb/in²
ISO Test
Charpy Impact Unnotched 4.50 J/cm²
21.4 ft-lb/in²
ISO 179
4.30 J/cm²

@Temperature -30.0 °C
20.5 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
ISO 179
0.700 J/cm²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Thermal Properties Metric English Comments
CTE, linear 20.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
11.1 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM Test
CTE, linear, Parallel to Flow 33.0 µm/m-°C
18.3 µin/in-°F
ISO 11359
CTE, linear, Transverse to Flow 75.0 µm/m-°C
41.7 µin/in-°F
ISO 11359
Melting Point 260 °C
500 °F
10 K/min
260 °C
500 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 250 °C
482 °F
ASTM Test
250 °C
482 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
ASTM Test
250 °C
482 °F
ISO 75
Vicat Softening Point 250 °C
482 °F
(50 °C/h / 50N) - B/50; ISO 306
Flammability, UL94 HB

@Thickness 1.66 mm
HB

@Thickness 0.0654 in
HB

@Thickness 0.810 mm
HB

@Thickness 0.0319 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Surface Resistance 1.00e+12 ohm
1.00e+12 ohm
IEC 60093
Dielectric Constant 3.5

@Frequency 1.00e+6 Hz
3.5

@Frequency 1.00e+6 Hz
IEC 60250
Dissipation Factor 0.014

@Frequency 100 Hz
0.014

@Frequency 100 Hz
IEC 60250
0.023

@Frequency 1.00e+6 Hz
0.023

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 550 V
550 V
IEC 60112
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
FDA 21 CFR 177.1500
Form Pellets
Impact Modified No
NSF Std. 51 Yes
Primary Processing Technique Injection Molding
Processing Injection Molding
Special characteristic Heat stabilized or stable to heat