Ineos ABS NOVODUR® P3T ABS, Injection Grade (discontinued **)

Category	Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ineos ABS NOVODUR® P3T ABS, Injection Grade (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Injection molding grade, higher heat resistance.Applications: Automotive industry.Information provided by the manufacturer.Novodur is produced by Styrolution (2014). This grade was discontinued prior to Styrolution's acquisition of the Novodur product line.

Physical Properties	Metric	English	Comments
Density	1.06 g/cc	0.0383 lb/in³
Water Absorption	0.30 %	0.30 %	Saturation in water
Water Absorption at Saturation	0.30 %	0.30 %
Melt Flow	2.0 g/10 min @Load 10.0 kg, Temperature 220 °C	2.0 g/10 min @Load 22.0 lb, Temperature 428 °F

Mechanical Properties	Metric	English
Tensile Strength, Yield	53.0 MPa	7690 psi
Elongation at Yield	2.8 %	2.8 %
Tensile Modulus	2.80 GPa	406 ksi
Charpy Impact Unnotched	NB	NB
	0.400 J/cm² @Temperature -30.0 °C	1.90 ft-lb/in² @Temperature -22.0 °F
Charpy Impact, Notched	1.20 J/cm²	5.71 ft-lb/in²
Tensile Creep Modulus, 1 hour	2500 MPa	363000 psi
Tensile Creep Modulus, 1000 hours	1900 MPa	276000 psi

Thermal Properties	Metric	English
CTE, linear, Parallel to Flow	80.0 µm/m-°C @Temperature 20.0 °C	44.4 µin/in-°F @Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	108 °C	226 °F
Deflection Temperature at 1.8 MPa (264 psi)	101 °C	214 °F
Vicat Softening Point	115 °C	239 °F
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in

Electrical Properties	Metric	English
Electrical Resistivity	1.00e+15 ohm-cm	1.00e+15 ohm-cm
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm
Dielectric Constant	2.9 @Frequency 1e+6 Hz	2.9 @Frequency 1e+6 Hz
	3.0 @Frequency 100 Hz	3.0 @Frequency 100 Hz
Dielectric Strength	33.0 kV/mm	838 kV/in
Dissipation Factor	0.0050 @Frequency 1e+6 Hz	0.0050 @Frequency 1e+6 Hz
	0.0060 @Frequency 100 Hz	0.0060 @Frequency 100 Hz
Comparative Tracking Index	600 V	600 V

Users viewing this material also viewed the following: