- Polymer Property : Melt Flow = 70 g/10 min
Polymer Property : Melt Flow = 70 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 70 g/10 min @Load 2.16 kg, Temperature 230 °C |
70 g/10 min @Load 4.76 lb, Temperature 446 °F |
Procedure A; ASTM D1238 |
| PolyOne Maxxam™ FR PP CONC 36 NAT S Polypropylene, Unspecified (PP, Unspecified) Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V.. |
|||
| Melt Flow | 70 g/10 min @Load 2.16 kg, Temperature 230 °C |
70 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| SABIC PP 413MNK45 Polypropylene Impact Copolymer for Injection Molding Product Description: PP 413MNK45 is a controlled rheology PP grade with a very high fluidity. It is provided with an antistatic package & nucleating agent and is especially developed for producing.. |
|||
| Melt Flow | 70 - 85 g/10 min @Load 2.16 kg, Temperature 210 °C |
70 - 85 g/10 min @Load 4.76 lb, Temperature 410 °F |
ASTM D1238 |
| NatureWorks® Ingeo™ 6251D Fiber Grade PLA NatureWorks® PLA polymer 6251D is a thermoplastic fiber-grade resin derived primarily from annually renewable resources. Available in pellet form, 6251D is designed for spunbond products using conv.. |
|||
| Melt Flow | 70 g/10 min | 70 g/10 min | ASTM D1238 |
| LyondellBasell Microthene® G MN71400 Low Density Polyethylene General DescriptionMicrothene G polyolefin powders are ground, irregularly-shaped particles designed for use in a broad range of specialty applications. Microthene G powders combine the unique prop.. |
|||
| Melt Flow | 70 g/10 min @Load 1.20 kg, Temperature 300 °C |
70 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| LG Chemical Lupoy 1080-70 Polycarbonate Resin Description: LUPOY PC 1080-70 resin is designed for optical media discs applications. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.Main Ch.. |
|||
| Melt Flow | 70 g/10 min @Load 2.16 kg, Temperature 230 °C |
70 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Ineos L70Z-01 Polypropylene Impact Copolymer L70Z-01 is a nucleated and antistatic high flow polypropylene medium impact copolymer for injection molding applications. This product meets the requirements of the U.S. Food and Drug Administration.. |
|||
| Melt Flow | 70 g/10 min @Load 5.00 kg, Temperature 266 °C |
70 g/10 min @Load 11.0 lb, Temperature 511 °F |
ASTM D1238 |
| SABIC Innovative Plastics Valox® 865 PBT (Europe-Africa-Middle East) VALOX 865 is a 30% glass fibre reinforced, non blooming flame retardant PBT+PET blend with an excellent surface appearance. Applications: External housings, steam irons, appliance housings and light.. |
|||
| Melt Flow | 70 g/10 min @Load 2.16 kg, Temperature 230 °C |
70 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Sanyo J-STAT 3180 Antistatic Additive Information provided by Tomen America, a US distributor of Pelestat. |
|||
| Melt Flow | 70 g/10 min @Load 2.16 kg, Temperature 235 °C |
70 g/10 min @Load 4.76 lb, Temperature 455 °F |
ASTM D1238R |
| UBE UBESTA® 3014U Rigid Electronic Grade Nylon 12 Description: UBESTA Nylon 12 has an excellent termite resistance than other plastics. UBESTA contributes as a material for jacket and sheath which lay for telephone and telegram Communication System.. |
|||
| Melt Flow | 70 g/10 min @Load 2.16 kg, Temperature 190 °C |
70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ AC-20531L UV Absorber Concentrate DescriptionPOLYBATCH® AC-20531L is a UV absorber concentrate containing 20% active additive based in low density polyethylene. POLYBATCH® AC-20531L is designed for use in polyethylene blown and c.. |
|||
| Melt Flow | 70 g/10 min @Load 2.16 kg, Temperature 190 °C |
70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ AC-20531L UV Absorber Concentrate DescriptionPOLYBATCH® AC-20531L is a UV absorber concentrate containing 20% active additive based in low density polyethylene. POLYBATCH® AC-20531L is designed for use in polyethylene blown and c.. |
|||
| Melt Flow | 70 g/10 min @Load 2.16 kg, Temperature 190 °C |
70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Total LDPE 1700 MN 18 C Low Density Polyethylene - Injection Molding and Compounding LDPE 1700 MN 18 C is a low density polyethylene made by a high pressure autoclave process without antioxidant. Grade for easy flow injection molding of flexible parts, powder production for grindin.. |
|||
| Melt Flow | 70 g/10 min @Load 2.16 kg, Temperature 230 °C |
70 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Total PPC 11712 Polypropylene, Heterophasic Copolymer ATOFINA Propylene 11712 is a nucleated controlled-rheology heterophasic copolymer. PPC 11712 is characterized by good stiffness and impact resistance as well as low shrinkage and low warpage. It h.. |
|||
| Melt Flow | 70 g/10 min @Load 2.16 kg, Temperature 230 °C |
70 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Total PPC 12642 Polypropylene, Heterophasic Copolymer, Injection Molding Polypropylene PPC 12642 is a nucleated antistatic heterophasic copolymer with high Melt Flow index of 70 g/10 min and good mechanical properties.Polypropylene PPC 10641 has been developed for high s.. |
|||
| Melt Flow | 70 g/10 min @Load 2.16 kg, Temperature 190 °C |
70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ AC-20531L UV Absorber Concentrate DescriptionPOLYBATCH® AC-20531L is a UV absorber concentrate containing 20% active additive based in low density polyethylene. POLYBATCH® AC-20531L is designed for use in polyethylene blown and c.. |
|||
| Melt Flow | 70 g/10 min @Load 2.16 kg, Temperature 190 °C |
70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ AC-20531L UV Absorber Concentrate DescriptionPOLYBATCH® AC-20531L is a UV absorber concentrate containing 20% active additive based in low density polyethylene. POLYBATCH® AC-20531L is designed for use in polyethylene blown and c.. |
|||
| Melt Flow | 70 g/10 min @Load 2.16 kg, Temperature 160 °C |
70 g/10 min @Load 4.76 lb, Temperature 320 °F |
cm<sup>3</sup>/10 min; ISO 1133 |
| EMS-Griltech Griltex® D 1500A Copolyamide Hotmelt Adhesive (Apparel Interlinings) Description: GRILTEX adhesive products, either in pellet or powdered form, are used to coat apparel interlining substrates. Interlining substrates, coated with GRILTEX adhesive products, provides fo.. |
|||
| Melt Flow | 70 g/10 min @Load 2.16 kg, Temperature 160 °C |
70 g/10 min @Load 4.76 lb, Temperature 320 °F |
cm<sup>3</sup>/10 min; ISO 1133 |
| EMS-Griltech Griltex® D 1500A Copolyamide Hotmelt Adhesive (Technical Applications) Description: GRILTEX adhesive products, either in pellet or powdered form, are used to coat apparel interlining substrates. Interlining substrates, coated with GRILTEX adhesive products, provides fo.. |
|||
| Melt Flow | 70 g/10 min @Load 2.16 kg, Temperature 160 °C |
70 g/10 min @Load 4.76 lb, Temperature 320 °F |
cm<sup>3</sup>/10 min; ISO 1133 |
| EMS-Griltech Griltex® D 1566A Heat Stabilized Copolyamide Hotmelt Adhesive (Apparel Interlinings) Description: GRILTEX adhesive products, either in pellet or powdered form, are used to coat apparel interlining substrates. Interlining substrates, coated with GRILTEX adhesive products, provides fo.. |
|||
| Melt Flow | 70 g/10 min @Load 2.16 kg, Temperature 160 °C |
70 g/10 min @Load 4.76 lb, Temperature 320 °F |
cm<sup>3</sup>/10 min; ISO 1133 |
| EMS-Griltech Griltex® D 1694A Copolyamide Hotmelt Adhesive (Apparel Interlinings) Description: GRILTEX adhesive products, either in pellet or powdered form, are used to coat apparel interlining substrates. Interlining substrates, coated with GRILTEX adhesive products, provides fo.. |
|||
| Melt Flow | 70 g/10 min @Load 5.00 kg, Temperature 280 °C |
70 g/10 min @Load 11.0 lb, Temperature 536 °F |
cm³/10min; ISO 1133 |
| DuPont Performance Polymers Rynite® RE19051 BK507 Polyethylene Terephthalate (PET) 40% Glass/Mineral Reinforced Flame Retardant Polyethylene Terephthalate Rynite RE19051 BK507 is a 40% glass and mineral reinforced flame retardant polyethylene terephthalate black resin.Information .. |
|||
| Melt Flow | 70 g/10 min @Load 10.0 kg, Temperature 220 °C |
70 g/10 min @Load 22.0 lb, Temperature 428 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Chi Mei Polylac® PA-756S ABS - High Flow Super high flow, medium impact |
|||
| Melt Flow | 70 g/10 min @Load 2.16 kg, Temperature 230 °C |
70 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Braskem TI4700P2 Impact Copolymer Polypropylene Description: Very high flexural modulus.Applications: Suggested uses include compounding, automotive interior trim, intricately designed parts, thinwalled parts, dairy containers, building and const.. |
|||
| Melt Flow | 70 g/10 min @Load 5.00 kg, Temperature 275 °C |
70 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Azoty Tarnow™ Tarnamid® T-27 MCS I Polyamide 6 - Impact Modified High impact resistance grade. Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main properties:H.. |
|||
| Melt Flow | 70 g/10 min @Load 2.16 kg, Temperature 190 °C |
70 g/10 min @Load 4.76 lb, Temperature 374 °F |
"E"; ASTM D1238 |
| Aaron Industries AAROPRENE® ATPR 1000 80A Elastomeric Compound AAROPRENE® ATPR 1000 Series Elastomeric CompoundDurometer values may be specified. Color may be specified. |
|||
| Melt Flow | 70 g/10 min | 70 g/10 min | ASTM D1238 |
| Huntsman PE2075 Injection Molding Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Very high flow rapid set-up characteristics, excellent clarity, and gloss.Applications: Injection molding: lids and difficult to fill applications.FDA Notes: .. |
|||
| Melt Flow | 70 g/10 min @Load 2.16 kg, Temperature 190 °C |
70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ AC-20531L UV Absorber Concentrate DescriptionPOLYBATCH® AC-20531L is a UV absorber concentrate containing 20% active additive based in low density polyethylene. POLYBATCH® AC-20531L is designed for use in polyethylene blown and c.. |
|||
| Melt Flow | 70 g/10 min @Load 2.16 kg, Temperature 230 °C |
70 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Multibase Multi-Flex® A 6221 CUV A Black TPE Thermoplastic Elastomer Forms: PelletsProcessing Methods:Injection Molding Information provided by Multibase |
|||
| Melt Flow | 70 g/10 min @Load 2.16 kg, Temperature 230 °C |
70 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Multibase Multi-Flex® A 6221 CUV A VY Dk Pewter TPO Thermoplastic Polyolefin Elastomer Forms: PelletsProcessing Methods:Injection MoldingInformation provided by Multibase |
|||
| Melt Flow | 70 g/10 min @Load 2.16 kg, Temperature 235 °C |
70 g/10 min @Load 4.76 lb, Temperature 455 °F |
ASTM D1238R |
| UBE UBESTA® P3014U Powder Electronic Grade Nylon 12 Description: UBESTA Nylon 12 has an excellent termite resistance than other plastics. UBESTA contributes as a material for jacket and sheath which lay for telephone and telegram Communication System.. |
|||