BASF Ultramid® A34 01 PA66 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® A34 01 PA66 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid A34 01 is an intermediate visosity, PA66 grade. It conforms to FDA requirements including, 21 CFR 177.1500,EU Directive 2002/72/EC, the German BfR recommendation "X Polyamide", 1.6.1998 or legislations for other countries will be provided on request.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Water Absorption 8.5 %
8.5 %
ISO 62
Moisture Absorption at Equilibrium 2.2 %
2.2 %
23°C/50% R.H.; ISO 62
Relative Viscosity 3.5 cP
3.5 cP
ISO Test; 96 % SAV
Viscosity Test 205 cm³/g
205 cm³/g
Viscosity number
Linear Mold Shrinkage 0.014 cm/cm
0.014 in/in
ASTM Data; MD
Melt Flow 40 g/10 min

@Load 5.00 kg,
Temperature 275 °C
40 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 80.0 MPa
11600 psi
50mm/min; ISO 527
80.0 MPa
11600 psi
2 in/min; ASTM Test
Elongation at Break 25 %
25 %
50mm/min, Nominal strain; ISO 527
50 %
50 %
2 in/min; ASTM Test
Elongation at Yield 4.2 %
4.2 %
50mm/min; ISO 527
Tensile Modulus 3.20 GPa
464 ksi
1mm/min; ISO 527
3.20 GPa
464 ksi
ASTM Test
Flexural Modulus 2.76 GPa
400 ksi
ASTM Test
Izod Impact, Notched 0.530 J/cm

@Temperature -40.0 °C
0.993 ft-lb/in

@Temperature -40.0 °F
ASTM Test
0.640 J/cm

@Thickness 3.17 mm
1.20 ft-lb/in

@Thickness 0.125 in
ASTM Test
Charpy Impact Unnotched NB
NB
ISO 179
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched NB
NB
ISO 179
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179
Thermal Properties Metric English Comments
CTE, linear 40.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
22.2 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM Test
CTE, linear, Parallel to Flow 85.0 µm/m-°C
47.2 µin/in-°F
ISO 11359
Melting Point 255 °C
491 °F
10 K/min
260 °C
500 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 199 °C
390 °F
ASTM Test
220 °C
428 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
167 °F
ISO 75
100 °C
212 °F
ASTM Test
Vicat Softening Point 250 °C
482 °F
(50 °C/h / 50N) - B/50; ISO 306
Flammability, UL94 V-2

@Thickness 1.57 mm
V-2

@Thickness 0.0618 in
V-2

@Thickness 0.890 mm
V-2

@Thickness 0.0350 in
Oxygen Index 28 %
28 %
ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz
3.2

@Frequency 1.00e+6 Hz
IEC 60250
3.8

@Frequency 100 Hz
3.8

@Frequency 100 Hz
IEC 60250
Dissipation Factor 0.0050

@Frequency 100 Hz
0.0050

@Frequency 100 Hz
IEC 60250
0.026

@Frequency 1.00e+6 Hz
0.026

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Descriptive Properties Value Comments
Color Natural
Commercial Status North America and Europe
FDA 21 CFR 177.1500
Form Pellets
Impact Modified No
Primary Processing Technique Film Extrusion
Processing Injection Molding
Other Extrusion