- Polymer Resources PPX-MF-FRG20 Modified-PPO, 40% Glass/Mineral Reinforced, Flame Retardant
Polymer Resources PPX-MF-FRG20 Modified-PPO, 40% Glass/Mineral Reinforced, Flame Retardant
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 40% Glass Filled , Polyphenylene Ether, Heat Resistant |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources PPX-MF-FRG20 Modified-PPO, 40% Glass/Mineral Reinforced, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Modified-Polyphenylene Oxide, 40% Glass/Mineral Reinforced, Flame RetardantFeatures: • Bromine Free • Chlorine Free • Self ExtinguishingProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D955 |
| Melt Flow | 1.0 - 9.0 g/10 min @Load 11.6 kg, Temperature 250 °C |
1.0 - 9.0 g/10 min @Load 25.6 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 90 | 90 | ASTM D785 |
| Tensile Strength at Break | 126 MPa | 18300 psi | ASTM D638 |
| Tensile Strength, Yield | 126 MPa | 18300 psi | ASTM D638 |
| Elongation at Yield | 1.5 % | 1.5 % | ASTM D638 |
| Flexural Strength | 159 MPa | 23000 psi | ASTM D790 |
| Flexural Modulus | 9.65 GPa | 1400 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm @Temperature 22.8 °C |
1.30 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C | 250 °F | ASTM D648 |
| Flammability, UL94 | V-1 @Thickness 1.59 mm |
V-1 @Thickness 0.0626 in |
|
| V-0 @Thickness 3.17 mm |
V-0 @Thickness 0.125 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 304 °C | 500 - 580 °F | |
| Middle Barrel Temperature | 271 - 310 °C | 520 - 590 °F | |
| Front Barrel Temperature | 282 - 316 °C | 540 - 600 °F | |
| Melt Temperature | 293 - 316 °C | 560 - 600 °F | |
| Mold Temperature | 76.7 - 104 °C | 170 - 220 °F | |
| Drying Temperature | 104 - 110 °C | 220 - 230 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0015 |
Users viewing this material also viewed the following:
- Neutrex Purgex™ 3057 Plus Purging Compound
- PolyOne Geon™ Vinyl Flexible R115AE Natural Polyvinyl Chloride, Flexible (PVC, Flexible)
- Lotte Chemical Titan TITANPRO® PD701 Polypropylene homopolymer
- Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1121°C, air cooled, aged 16 hours at 899°C
- SABIC Innovative Plastics LNP THERMOCOMP UX04509 PPA (Asia Pacific)
- A. Schulman FORMION™ FI 234 20% Mineral Reinforced Ionomer / Nylon Alloy
- ExxonMobil Mobil Avrex S Turbo 256
- Clariant Renol PA113 Nylon 66, Heat Stabilized, Lubricated
- Amity Thermosets ATS 166 Phenolic Molding Chopped cotton fabric Filler, Compression Molded
- Beijing Ranger Chem PBT-201-G30 272 Flame Retarding FR PBT
Copyright © lookpolymers.com All Rights Reserved