BASF Ultramid® 8253 HS PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8253 HS PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8253 HS is a heat stabilized, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications requiring improved dry as molded toughness and increased flexibility. It is also available in non-heat stabilized (Ultramid 8253) and/or pigmented versions.
Physical Properties Metric English Comments
Water Absorption 1.5 %
1.5 %
24 hour; ISO Test
Linear Mold Shrinkage 0.012 cm/cm
0.012 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Hardness, Rockwell R 82
82
ASTM Test
Tensile Strength at Break 60.0 MPa
8700 psi
0.2 in/min; ASTM Test
100 MPa

@Temperature -40.0 °C
14500 psi

@Temperature -40.0 °F
ASTM Test
100 MPa

@Temperature -40.0 °C
14500 psi

@Temperature -40.0 °F
ISO Data
Tensile Strength, Yield 65.0 MPa
9430 psi
2 in/min; ASTM Test
20.0 MPa

@Temperature 120 °C
2900 psi

@Temperature 248 °F
ASTM Test
20.0 MPa

@Temperature 120 °C
2900 psi

@Temperature 248 °F
ISO Data
25.0 MPa

@Temperature 80.0 °C
3630 psi

@Temperature 176 °F
ISO Data
25.0 MPa

@Temperature 80.0 °C
3630 psi

@Temperature 176 °F
ASTM Test
117 MPa

@Temperature -40.0 °C
17000 psi

@Temperature -40.0 °F
ASTM Test
117 MPa

@Temperature -40.0 °C
17000 psi

@Temperature -40.0 °F
ISO Data
Elongation at Break >= 100 %
>= 100 %
2 in/min; ASTM Test
9.0 %

@Temperature -40.0 °C
9.0 %

@Temperature -40.0 °F
ASTM Test
9.0 %

@Temperature -40.0 °C
9.0 %

@Temperature -40.0 °F
ISO Data
Elongation at Yield 4.0 %
4.0 %
2 in/min; ASTM Test
7.0 %

@Temperature -40.0 °C
7.0 %

@Temperature -40.0 °F
ASTM Test
7.0 %

@Temperature -40.0 °C
7.0 %

@Temperature -40.0 °F
ISO Data
29 %

@Temperature 80.0 °C
29 %

@Temperature 176 °F
ISO Data
29 %

@Temperature 80.0 °C
29 %

@Temperature 176 °F
ASTM Test
34 %

@Temperature 120 °C
34 %

@Temperature 248 °F
ASTM Test
34 %

@Temperature 120 °C
34 %

@Temperature 248 °F
ISO Data
Tensile Modulus 0.295 GPa

@Temperature 120 °C
42.8 ksi

@Temperature 248 °F
ISO Data
0.400 GPa

@Temperature 80.0 °C
58.0 ksi

@Temperature 176 °F
ISO Data
2.835 GPa

@Temperature -40.0 °C
411.2 ksi

@Temperature -40.0 °F
ISO Data
Flexural Strength 65.0 MPa
9430 psi
ISO Data
87.0 MPa
12600 psi
ASTM Test
14.0 MPa

@Temperature 120 °C
2030 psi

@Temperature 248 °F
ASTM Test
20.0 MPa

@Temperature 93.0 °C
2900 psi

@Temperature 199 °F
ASTM Test
25.0 MPa

@Temperature 65.0 °C
3630 psi

@Temperature 149 °F
ASTM Test
148 MPa

@Temperature -40.0 °C
21500 psi

@Temperature -40.0 °F
ASTM Test
Flexural Modulus 1.90 GPa
276 ksi
ISO Data
2.21 GPa
321 ksi
ASTM Test
0.260 GPa

@Temperature 120 °C
37.7 ksi

@Temperature 248 °F
ASTM Test
0.325 GPa

@Temperature 93.0 °C
47.1 ksi

@Temperature 199 °F
ASTM Test
0.415 GPa

@Temperature 65.0 °C
60.2 ksi

@Temperature 149 °F
ASTM Test
Izod Impact, Notched 0.800 J/cm

@Temperature -40.0 °C
1.50 ft-lb/in

@Temperature -40.0 °F
ASTM Test
1.48 J/cm

@Thickness 3.17 mm
2.77 ft-lb/in

@Thickness 0.125 in
ASTM Test
Thermal Properties Metric English Comments
CTE, linear 99.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
55.0 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM Test
Melting Point 220 °C
428 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 168 °C
334 °F
ASTM Test
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
ASTM Test
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Impact Modified Yes
Primary Processing Technique Injection Molding
UL.UL-C Yes