BASF Ultramid® 8231G HS 14% Glass Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8231G HS 14% Glass Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8231G HS is a heat stabilized, 14% glass fiber reinforced nylon 6 injection molding compound. It is also available in non-heat stabilized (Ultramid 8231) and/or pigmented versions. The glass fiber reinforcement enhances performance such as strength, stiffness and heat deflection temperature. The heat stabilizer system extends the properties at elevated temperatures. It also has excellent chemical resistance to greases, oils and hydrocarbons. njection molding compound possessing a balance of engineering properties combined with excellent processability and surface aesthetics.
Physical Properties Metric English Comments
Density 1.067 g/cc
0.03855 lb/in³
Melt; ISO 1183
1.23 g/cc
0.0444 lb/in³
ISO 1183
Water Absorption 1.4 %
1.4 %
24 hour; ISO Test
8.1 %
8.1 %
ISO 62
Moisture Absorption at Equilibrium 2.3 %
2.3 %
23°C/50% R.H.; ISO 62
Viscosity Measurement 50
50
Formic Acid
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Hardness, Rockwell R 121
121
ASTM Test
Tensile Strength at Break 140 MPa
20300 psi
0.2 in/min; ASTM Test
50.0 MPa

@Temperature 120 °C
7250 psi

@Temperature 248 °F
ISO Data
50.0 MPa

@Temperature 120 °C
7250 psi

@Temperature 248 °F
ASTM Test
60.0 MPa

@Temperature 80.0 °C
8700 psi

@Temperature 176 °F
ASTM Test
60.0 MPa

@Temperature 80.0 °C
8700 psi

@Temperature 176 °F
ISO Data
160 MPa

@Temperature -40.0 °C
23200 psi

@Temperature -40.0 °F
ISO Data
160 MPa

@Temperature -40.0 °C
23200 psi

@Temperature -40.0 °F
ASTM Test
Tensile Strength, Ultimate 140 MPa
20300 psi
5mm/min; ISO 527
Elongation at Break 4.0 %
4.0 %
5mm/min; ISO 527
4.0 %
4.0 %
0.2 in/min; ASTM Test
3.0 %

@Temperature -40.0 °C
3.0 %

@Temperature -40.0 °F
ASTM Test
3.0 %

@Temperature -40.0 °C
3.0 %

@Temperature -40.0 °F
ISO Data
7.0 %

@Temperature 120 °C
7.0 %

@Temperature 248 °F
ISO Data
7.0 %

@Temperature 120 °C
7.0 %

@Temperature 248 °F
ASTM Test
8.0 %

@Temperature 80.0 °C
8.0 %

@Temperature 176 °F
ASTM Test
8.0 %

@Temperature 80.0 °C
8.0 %

@Temperature 176 °F
ISO Data
Tensile Modulus 5.96 GPa
864 ksi
1mm/min; ISO 527
2.09 GPa

@Temperature 120 °C
303 ksi

@Temperature 248 °F
ISO Data
2.47 GPa

@Temperature 80.0 °C
358 ksi

@Temperature 176 °F
ISO Data
5.95 GPa

@Temperature -40.0 °C
863 ksi

@Temperature -40.0 °F
ISO Data
Flexural Strength 160 MPa
23200 psi
ISO Data
172 MPa
24900 psi
ASTM Test
76.0 MPa

@Temperature 120 °C
11000 psi

@Temperature 248 °F
ASTM Test
90.0 MPa

@Temperature 93.0 °C
13100 psi

@Temperature 199 °F
ASTM Test
110 MPa

@Temperature 65.0 °C
16000 psi

@Temperature 149 °F
ASTM Test
214 MPa

@Temperature -40.0 °C
31000 psi

@Temperature -40.0 °F
ASTM Test
Flexural Modulus 4.77 GPa
692 ksi
ISO Data
5.31 GPa
770 ksi
ASTM Test
1.93 GPa

@Temperature 120 °C
280 ksi

@Temperature 248 °F
ASTM Test
2.40 GPa

@Temperature 65.0 °C
348 ksi

@Temperature 149 °F
ASTM Test
Izod Impact, Notched 0.590 J/cm

@Thickness 3.17 mm
1.11 ft-lb/in

@Thickness 0.125 in
ASTM Test
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
ISO Test
Charpy Impact Unnotched 4.00 J/cm²
19.0 ft-lb/in²
ISO 179
Charpy Impact, Notched 0.650 J/cm²
3.09 ft-lb/in²
ISO 179
0.550 J/cm²

@Temperature -30.0 °C
2.62 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Thermal Properties Metric English Comments
CTE, linear 50.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
27.8 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM Test
CTE, linear, Parallel to Flow 39.0 µm/m-°C
21.7 µin/in-°F
ISO 11359
CTE, linear, Transverse to Flow 78.0 µm/m-°C
43.3 µin/in-°F
ISO 11359
Specific Heat Capacity 2.728 J/g-°C
0.6520 BTU/lb-°F
Melt
Thermal Conductivity 0.230 W/m-K
1.60 BTU-in/hr-ft²-°F
Melt
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 217 °C
423 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 195 °C
383 °F
ISO 75
200 °C
392 °F
ASTM Test
Flammability, UL94 HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 3.4

@Frequency 1.00e+6 Hz
3.4

@Frequency 1.00e+6 Hz
IEC 60250
3.6

@Frequency 100 Hz
3.6

@Frequency 100 Hz
IEC 60250
3.7

@Frequency 1.00e+6 Hz
3.7

@Frequency 1.00e+6 Hz
ASTM Data
4.0

@Frequency 1e+9 Hz
4.0

@Frequency 1e+9 Hz
ASTM Data
Dielectric Strength 40.0 kV/mm
1020 kV/in
IEC 60243-1
Dissipation Factor 0.010

@Frequency 1e+9 Hz
0.010

@Frequency 1e+9 Hz
ASTM Data
0.010

@Frequency 1.00e+6 Hz
0.010

@Frequency 1.00e+6 Hz
ASTM Data
0.010

@Frequency 100 Hz
0.010

@Frequency 100 Hz
IEC 60250
0.020

@Frequency 1.00e+6 Hz
0.020

@Frequency 1.00e+6 Hz
IEC 60250
Processing Properties Metric English Comments
Melt Temperature 275 °C
527 °F
Injection molding
Mold Temperature 95.0 °C
203 °F
Injection molding
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
Special characteristic Heat stabilized or stable to heat
UL.UL-C Yes