Multibase Multi-ABS 801 Natural Extrusion Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded |
| Manufacturer | Multibase |
| Trade Name | Multi-ABS |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-ABS 801 Natural Extrusion Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Multibase.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792-91 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955-89 |
| Melt Flow | 2.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D-1238-94a |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 96 | 96 | ASTM D785-95 |
| Tensile Strength, Ultimate | 44.8 MPa | 6500 psi | ASTM D638-95 |
| Elongation at Break | 15 % | 15 % | ASTM D638-95 |
| Flexural Strength | 63.8 MPa | 9250 psi | ASTM D790-95 |
| Flexural Modulus | 2.31 GPa | 335 ksi | RT; ASTM D-790-95 |
| Izod Impact, Notched | 3.74 J/cm | 7.01 ft-lb/in | ASTM D256-93a |
| Gardner Impact | 12.4 J | 9.15 ft-lb | ASTM D5420-93 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C | 181 °F | injection molded unannealed; ASTM D-648-95 |
| 98.0 °C | 208 °F | injection molded annealed; ASTM D-648-95 | |
| Vicat Softening Point | 92.0 °C | 198 °F | ASTM D1525-95 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
Users viewing this material also viewed the following:
- MV Labs SM800 Sm2O3 Samarium oxide
- Polymax® Maxelast® P3770 TPE, PP Overmold or Standalone use
- Lanxess Durethan® ECO BV 35 H2 900500 Nylon 6, 35% Glass Fiber
- Samsung Cheil Industries Starex® HG-0760AT ABS, Unreinforced
- Styron Magnumâ„¢ 9450P ABS, High Gloss
- Zeon Chemicals Quintone® K100 Aliphatic Hydrocarbon Resin
- Addiplast Addilene H 490 S Flame Retardant Polypropylene
- Arlon LW201Xxx-M1 0.020" (0.508 mm) Self-Fusing Silicone Tape (Triangular, Unsupported) with Mylar Interleave
- Plastcom SLOVALEN PH 73 T 20 PP, 20% mineral filling
- Formosa Plastics Formolene® 1102K Cast and BOPP Film Polypropylene
Copyright © lookpolymers.com All Rights Reserved