Arlon AD350A PTFE/Woven Fiberglass/Ceramic Filled Composite

Category Polymer , Thermoplastic , Fluoropolymer , PTFE
Manufacturer Arlon
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon AD350A PTFE/Woven Fiberglass/Ceramic Filled Composite.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Tighter Dielectric Tolerance Low Z-Axis Thermal ExpansionCeramic Filled PTFEHigh Thermal ConductivityLarge Panel SizeBenefits:Higher Consistency of PerformanceSuperior PTH AdhesionHeat Dissipation and ManagementMultiple boards per panel; Larger Printed Circuit Board formatsTypical Applications:High Power ApplicationsLow Noise Amplifiers (LNAs)Low Noise Blocks (LNBs)Filters and CouplersInformation provided by Arlon Materials for Electronics (MED).
Physical Properties Metric English Comments
Density 2.10 g/cc
0.0759 lb/in³
ASTM D792 Method A
Water Absorption 0.10 %
0.10 %
IPC TM-650 2.6.2.2
Outgassing - Total Mass Loss 0.00 %

@Pressure <=1.33e-10 MPa,
Temperature 125 °C
0.00 %

@Pressure <=1.93e-8 psi,
Temperature 257 °F
Water Vapor Recovered; NASA SP-R-0022A
0.020 %

@Pressure <=1.33e-10 MPa,
Temperature 125 °C
0.020 %

@Pressure <=1.93e-8 psi,
Temperature 257 °F
Collected Volatiles; NASA SP-R-0022A
0.020 %

@Pressure <=1.33e-10 MPa,
Temperature 125 °C
0.020 %

@Pressure <=1.93e-8 psi,
Temperature 257 °F
NASA SP-R-0022A
Mechanical Properties Metric English Comments
Tensile Strength >= 138 MPa
>= 20000 psi
IPC TM-650 2.4.18
Modulus of Elasticity >= 4.83 GPa
>= 700 ksi
ASTM D638
Flexural Modulus >= 3.72 GPa
>= 540 ksi
ASTM D790
Compressive Modulus >= 2.41 GPa
>= 350 ksi
ASTM D695
Peel Strength 2.63 kN/m
15.0 pli
To Copper (1/2 oz.); A, TS; IPC TM-650 2.4.8
2.98 kN/m
17.0 pli
To Copper (1 oz.); A, TS; IPC TM-650 2.4.8
Thermal Properties Metric English Comments
CTE, linear 5.00 µm/m-°C

@Temperature 0.000 - 100 °C
2.78 µin/in-°F

@Temperature 32.0 - 212 °F
x direction; IPC TM-650 2.4.24
9.00 µm/m-°C

@Temperature 0.000 - 100 °C
5.00 µin/in-°F

@Temperature 32.0 - 212 °F
y direction; IPC TM-650 2.4.24
CTE, linear, Transverse to Flow 35.0 µm/m-°C

@Temperature 0.000 - 100 °C
19.4 µin/in-°F

@Temperature 32.0 - 212 °F
z direction; IPC TM-650 2.4.24
Thermal Conductivity 0.450 W/m-K

@Temperature 100 °C
3.12 BTU-in/hr-ft²-°F

@Temperature 212 °F
ASTM E1225
Flammability, UL94 V-0
V-0
Vertical Burn
Electrical Properties Metric English Comments
Volume Resistivity 1.20e+15 ohm-cm
1.20e+15 ohm-cm
C96/35/90; IPC TM-650 2.5.17.1
Surface Resistance 4.50e+13 ohm
4.50e+13 ohm
C96/35/90; IPC TM-650 2.5.17.1
Dielectric Constant 3.45 - 3.55

@Frequency 1.00e+10 Hz
3.45 - 3.55

@Frequency 1.00e+10 Hz
C23/50; IPC TM-650 2.5.5.5
Dielectric Breakdown >= 45000 V
>= 45000 V
D48/50; ASTM D149
Dissipation Factor 0.0030

@Frequency 1.00e+10 Hz
0.0030

@Frequency 1.00e+10 Hz
C23/50; IPC TM-650 2.5.5.5
Arc Resistance >= 180 sec
>= 180 sec
D48/50; IPC TM-650 2.5.1B
Descriptive Properties Value Comments
Temperature Coefficient of Dielectric (ppm/°C) -55
IPC TM-650 2.5.5.5; at 10 GHz (-40 - 150°C)