Lehmann & Voss LUVOCOM® 1100-7337/WT Polyether sulfone, unreinforced
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1100-7337/WT Polyether sulfone, unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Apparatus- and precision engineering, film- and photo industry, sporting- and leisure goods, medical- and electrical enineering, aircraft- and aerospace industry.High dimensionally stable precision parts, even at elevated temperatures and narrow tolerance range.Superheated steam sterilizable.Inherent flame resistance.High quality terminal bar, switches and plugs, relais, lamp reflectors, sterilizable medical equipment.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 90.0 MPa | 13100 psi | |
| Elongation at Yield | 6.2 % | 6.2 % | |
| 8.0 % | 8.0 % | flexural | |
| Modulus of Elasticity | 3.10 GPa | 450 ksi | |
| Flexural Strength | 130 MPa | 18900 psi | |
| Flexural Modulus | 2.60 GPa | 377 ksi | |
| Charpy Impact Unnotched | 9.50 J/cm² | 45.2 ft-lb/in² | flatwise; ISO 179 1fU |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179 1eA |
| Coefficient of Friction, Dynamic | 0.34 | 0.34 | |
| Coefficient of Friction, Static | 0.28 | 0.28 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 55.0 µm/m-°C | 30.6 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 180 °C | 356 °F | |
| 220 °C | 428 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | |
| Vicat Softening Point | 215 °C | 419 °F | DIN ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 350 °C | 662 °F | mass temp |
| Nozzle Temperature | 340 - 360 °C | 644 - 680 °F | |
| Zone 1 | 355 - 375 °C | 671 - 707 °F | |
| Zone 2 | 360 - 380 °C | 680 - 716 °F | |
| Zone 3 | 350 - 370 °C | 662 - 698 °F | |
| Mold Temperature | 120 - 200 °C | 248 - 392 °F | |
| Drying Temperature | 150 °C @Time 10800 - 18000 sec |
302 °F @Time 3.00 - 5.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | signal white |
Users viewing this material also viewed the following:
- PolyOne Dynaflex™ G6713-0001 Thermoplastic Elastomer (TPE)
- RheTech Products G20P100-601 20% Glass Fiber Reinforced Polypropylene, UV Stabilized, (Ford ZUA5) Dark Graphite
- GRECO ISOTHANE 3080AF Polyether TPU Resin
- Solvay TECHNYL® A 218 V35 PA66, 35% glass fiber, Conditioned
- SABIC Innovative Plastics LNP LUBRICOMP WFP36 PBT
- SABIC Innovative Plastics LNP THERMOCOMP RF006S PA 66
- Entec Hypro™ PP-HP35NS Homopolymer, 35 Melt Flow, Nucleated, Anti-stat
- Huntsman Rexell® V3101 Blown Film Extrusion LLDPE (discontinued **)
- SABIC Innovative Plastics LNP THERMOCOMP DX06409 PC (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved