BASF Ultraform® N2640 E4 POM
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | BASF |
| Trade Name | Ultraform® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultraform® N2640 E4 POM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Is a POM + MBS, elastomer-modified injection-molding grade with high toughness and high weld line strength.Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Water Absorption | 0.90 % | 0.90 % | Saturation; ISO 62 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C; 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.018 cm/cm | 0.018 in/in | ISO 2577 |
| Linear Mold Shrinkage, Transverse | 0.018 cm/cm | 0.018 in/in | ISO 2577 |
| Melt Flow | 3.9 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.9 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 88.0 MPa @Load 36.5 kg, Time 30.0 sec |
12800 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | 50 mm/min; ISO 527-2 |
| Elongation at Break | >= 50 % | >= 50 % | Nominal, 50 mm/min; ISO 527-2 |
| Elongation at Yield | 7.3 % | 7.3 % | 50 mm/min; ISO 527-2 |
| Modulus of Elasticity | 1.70 GPa | 247 ksi | ISO 527-2 |
| Charpy Impact Unnotched | 24.0 J/cm² @Temperature -30.0 °C |
114 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.850 J/cm² @Temperature -30.0 °C |
4.04 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 140 µm/m-°C @Temperature 23.0 - 55.0 °C |
77.8 µin/in-°F @Temperature 73.4 - 131 °F |
DIN 53752 |
| Melting Point | 166 °C | 331 °F | DIN 53765 |
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75-2 |
| Vicat Softening Point | 125 °C | 257 °F | ISO 306 |
| Decomposition Temperature | >= 240 °C | >= 464 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.4 @Frequency 1.00e+6 Hz |
3.4 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.5 @Frequency 100 Hz |
3.5 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 37.0 kV/mm | 940 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0030 @Frequency 100 Hz |
0.0030 @Frequency 100 Hz |
IEC 60250 |
| 0.0080 @Frequency 1.00e+6 Hz |
0.0080 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 |
| 600 V | 600 V | Test solution B; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 °C | 392 °F | Hopper Throat |
| Zone 1 | 200 °C | 392 °F | Feed zone |
| Zone 2 | 200 °C | 392 °F | Compression |
| Zone 3 | 200 °C | 392 °F | Metering-zone |
| Zone 4 | 200 °C | 392 °F | Nozzle |
| Melt Temperature | 200 °C | 392 °F | Optimal |
| 190 - 220 °C | 374 - 428 °F | Injection-molding | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Injection-molding |
| 80.0 °C | 176 °F | Optimal |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Commercial Status | Europe | |
| Ignition Temperature | 320 - 340°C | ASTM D1929 |
| Peripheral screw speed | <0.3 m/s | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- Plaskolite West Optix® CA-1000 IG UC Clear High Impact Acrylic Resin
- Eastman Tenite 371A-12 CAP Cellulose Acetate Propionate (discontinued **)
- LG Chemical Lupoy 1300-22 Polycarbonate Resin
- Schwartz Technical Plastics LAMIGAMID® 319 Cast Polyamide 6, Oil Filled, Dry
- Techmer ES HiFill FR® PA6/6 GF33 FR HS L 15% Carbon Filled
- A. Schulman POLYBATCH™ Red LL50283/3 Concentrate Based In LLDPE
- 3M CN-3490 EMI Shielding Tape
- BASF Procom® D 1165 Polypropylene
- Braskem BS600 HDPE Blow Molding Polyethylene Copolymer
Copyright © lookpolymers.com All Rights Reserved