BASF Ultradur® B 4300 G6 HR 30% Glass Filled PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultradur®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultradur® B 4300 G6 HR 30% Glass Filled PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Is a PBT, injection-molding grade with 30% glass fibers; for rigid and dimensionally stable technical parts with increased requirements on hydrolysis resistance, e.g. automotive connectors and housings for electronic units under the hood.Information provided by BASF
Physical Properties Metric English Comments
Density 1.51 g/cc
0.0546 lb/in³
ISO 1183
Water Absorption 0.40 %
0.40 %
Saturation; DIN 53495/1L
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C; 50% RH
Viscosity Measurement 108
108
[ml/g]; Viscosity number; ISO 1628
Linear Mold Shrinkage, Flow 0.0045 cm/cm
0.0045 in/in
60x60x2 mm; ISO 294
Linear Mold Shrinkage, Transverse 0.013 cm/cm
0.013 in/in
60x60x2 mm; ISO 294
Mechanical Properties Metric English Comments
Tensile Strength, Yield 130 MPa
18900 psi
50 mm/min; ISO 527-2
Elongation at Break 3.3 %
3.3 %
50mm/min; ISO 527-2
Modulus of Elasticity 8.70 GPa
1260 ksi
ISO 527-2
Charpy Impact Unnotched 7.00 J/cm²
33.3 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 1.20 J/cm²
5.71 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 220 - 225 °C
428 - 437 °F
DSC; ISO 11357-3
Maximum Service Temperature, Air 210 °C
410 °F
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
ISO 75-2
Processing Properties Metric English Comments
Melt Temperature 250 - 275 °C
482 - 527 °F
Injection-molding
Mold Temperature 60.0 - 100 °C
140 - 212 °F
Descriptive Properties Value Comments
Color Natural and Black
Commercial Status Europe
Primary Processing Technique Injection Molding