SABIC Innovative Plastics Cycoloy® IP1000 PC+ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycoloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycoloy® IP1000 PC+ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Automotive applications: High impact and ductility to -22F for interior trim and instrument panel applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 13.5 g/10 min @Load 5.00 kg, Temperature 260 °C |
13.5 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 54.0 MPa | 7830 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 120 % | 120 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.20 GPa | 319 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 85.0 MPa | 12300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.23 GPa | 323 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 6.70 J/cm | 12.6 ft-lb/in | ASTM D256 |
| 5.00 J/cm @Temperature -30.0 °C |
9.37 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Dart Drop, Total Energy | 50.0 J @Temperature 23.0 °C |
36.9 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| 56.0 J @Temperature -30.0 °C |
41.3 ft-lb @Temperature -22.0 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 129 °C @Thickness 3.20 mm |
264 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C @Thickness 3.20 mm |
226 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 126 °C | 259 °F | Rate B/50; ASTM D1525 |
Users viewing this material also viewed the following:
- PolyOne Nymax™ 1200 A HS Black 13 A Polyamide 66 (Nylon 66)
- Overview of materials for Polyphthalamide (PPA), High Impact
- Lucent Polymers PBT-310 Polybutylene Terephthalate, 30% Glass Fiber/Mineral Reinforced, Low Warp
- Haynes Ultimet® alloy, aged 1000 hours at 982°C
- Samyang Trirex® PC-3025IR 10 MFI Clear Polycarbonate With Release
- SABIC Innovative Plastics LNP Stat-loy W3000 PBT
- Loctite® 3872 1 component acrylic/urethane UV/Heat Cure Flexible Adhesive
- Diamond Polymers NPP 808 C2 TDS Polycarbonate Alloy, Natural
- Clariant Renol PA1SP0019 Nylon 66/PPS Alloy, 20% Glass, 20% Mineral
- Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 10 hours at 649°C (1200°F)
Copyright © lookpolymers.com All Rights Reserved