Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Filled, Impact Grade |
Manufacturer | Azoty Tarnow™ (Zaklady Azotowe) |
Trade Name | Tarnamid® |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Azoty Tarnow™ Tarnamid® T-27 GF15 I Polyamide 6 - Glass Fiber Reinforced.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.20 g/cc | 1.20 g/cc | ISO 1183 |
Water Absorption | 2.3 % @Time 86400 sec |
2.3 % @Time 24.0 hour |
ISO 62 |
Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | ISO 294-4 |
Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | ISO 294-4 |
Melt Flow | 45 g/10 min @Load 5.00 kg, Temperature 275 °C |
45 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Ball Indentation Hardness | 80.0 MPa @Load 36.5 kg |
11600 psi @Load 80.5 lb |
cond.; ISO 2039-1 |
160 MPa @Load 36.5 kg |
23200 psi @Load 80.5 lb |
dry; ISO 2039-1 | |
Tensile Strength | 75.0 MPa | 10900 psi | cond.; ISO 527 |
100 MPa | 14500 psi | dry; ISO 527 | |
Elongation at Break | 5.0 % | 5.0 % | dry; ISO 527 |
8.0 % | 8.0 % | cond.; ISO 527 | |
Tensile Modulus | 3.00 GPa | 435 ksi | cond.; ISO 527 |
5.50 GPa | 798 ksi | dry; ISO 527 | |
Flexural Strength | <= 160 MPa | <= 23200 psi | dry, 3.5% flexure; ISO 178 |
Flexural Modulus | 4.50 GPa | 653 ksi | dry; ISO 178 |
Charpy Impact Unnotched | 7.50 J/cm² | 35.7 ft-lb/in² | dry; ISO 179 1eU |
8.50 J/cm² | 40.4 ft-lb/in² | cond.; ISO 179 1eU | |
Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | dry; ISO 179 1eA |
2.00 J/cm² | 9.52 ft-lb/in² | cond.; ISO 179 1eA |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Melting Point | 221 °C | 430 °F | |
Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | dry; ISO 75 |
Vicat Softening Point | 200 °C @Load 5.10 kg |
392 °F @Load 11.2 lb |
dry; ISO 306 |
Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
Glow Wire Test | 550 °C @Thickness 2.00 mm |
1020 °F @Thickness 0.0787 in |
PN-EN-60695-2-12 |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 93 |
Dielectric Strength | 22.0 kV/mm | 559 kV/in | IEC 243-1 |
Comparative Tracking Index | 600 V | 600 V | IEC 112 |
Processing Properties | Metric | English | Comments |
---|---|---|---|
Melt Temperature | 230 - 290 °C | 446 - 554 °F | |
Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | 80 - 90°C is recommended |
Drying Temperature | 75.0 - 100 °C @Time 7200 - 14400 sec |
167 - 212 °F @Time 2.00 - 4.00 hour |
|
Moisture Content | <= 0.10 % | <= 0.10 % | |
Injection Pressure | 80.0 - 130 MPa | 11600 - 18900 psi | 80 MPa is recommended |