Asia International Enterprise (Hong Kong) ST60G6 Nylon 66, 30% Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Asia Int'l Enterprise (Hong Kong) Limited |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asia International Enterprise (Hong Kong) ST60G6 Nylon 66, 30% Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asia International Enterprise (Hong Kong) Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc @Temperature 23.0 °C |
1.36 g/cc @Temperature 73.4 °F |
ASTM D792 |
| Filler Content | 30 % | 30 % | |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Ultimate | 196 MPa | 28400 psi | 5mm/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | 5mm/min; ASTM D638 |
| Flexural Strength | 275 MPa | 39900 psi | 2.8mm/min; ASTM D790 |
| Flexural Modulus | 5.88 GPa | 853 ksi | 2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 2.45 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
4.59 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 250 - 300 °C | 482 - 572 °F | Cylinder Temperature |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour |
Users viewing this material also viewed the following:
- Omni Plastics OmniTuff™ CPP CCF20 Copolymer Polypropylene Calcium Carbonate Filled
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, 400ºF Cure Temperature
- LG Chemical LS170 PVC
- Saint-Gobain CHR® TH Skived PTFE Film Backing Silicone Adhesive Pressure Sensitive Tape
- Solvay TECHNYL® 2912GMH7-P PA66, 63% glass fiber, DRY
- CoorsTek Nitrogen Bonded Silicon Carbide, SCNB
- Aremco Ceramabind™ 643-2 High Temperature Inorganic Binder
- E-Polymers EFLEX® S1050 General
- Overview of materials for Polyethersulfone, Carbon Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved