Asia International Enterprise (Hong Kong) 60G2-13GF Nylon 66, 13% Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled |
| Manufacturer | Asia Int'l Enterprise (Hong Kong) Limited |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asia International Enterprise (Hong Kong) 60G2-13GF Nylon 66, 13% Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asia International Enterprise (Hong Kong) Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc @Temperature 23.0 °C |
1.22 g/cc @Temperature 73.4 °F |
ASTM D792 |
| Filler Content | 13 % | 13 % | |
| Linear Mold Shrinkage | 0.0060 - 0.012 cm/cm | 0.0060 - 0.012 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength, Ultimate | 124 MPa | 17900 psi | 5mm/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ASTM D638 |
| Flexural Strength | 167 MPa | 24200 psi | 2.8mm/min; ASTM D790 |
| Flexural Modulus | 4.81 GPa | 697 ksi | 2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
0.918 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 261 °C | 502 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 242 °C | 468 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 250 - 300 °C | 482 - 572 °F | Cylinder Temperature |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® IM1063 PC (Europe-Africa-Middle East)
- PolyOne Geon™ Vinyl Flexible R276AE Polyvinyl Chloride, Flexible (PVC, Flexible)
- EMS-Grivory Grivory® 2S 20 nat PA610
- Eurostar Starflam PZ00062E PA6, Glass Fiber Filled, Flame Retardant, Injection Molded
- BNZ Materials BNZP-25L Insulating Firebrick (French Grade)
- ATI Allegheny Ludlum AL 29-4-2® Duplex Stainless Steel, UNS S44800
- 3M Dyneon™ PVDF 11008/0001 Polyvinylidene Fluoride
- A. Schulman ComAlloy Hiloy® 513 Polycarbonate, Glass Reinforced, UL
- AK Steel ASTM A 1011, Class 2 Formable, Grade 60K Hot Rolled Carbon Steel, Medium/High Strength Low Alloy Steel (HSLA)
- Karina E 840-10/176-CRA White PVC Compound
Copyright © lookpolymers.com All Rights Reserved