Asia International Enterprise (Hong Kong) 6010FGN Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Asia Int'l Enterprise (Hong Kong) Limited |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asia International Enterprise (Hong Kong) 6010FGN Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asia International Enterprise (Hong Kong) Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc @Temperature 23.0 °C |
1.15 g/cc @Temperature 73.4 °F |
ASTM D792 |
| Filler Content | 0.00 % | 0.00 % | |
| Linear Mold Shrinkage | 0.0090 - 0.017 cm/cm | 0.0090 - 0.017 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Ultimate | 76.5 MPa | 11100 psi | 5mm/min; ASTM D638 |
| Elongation at Break | 35 % | 35 % | 5mm/min; ASTM D638 |
| Flexural Strength | 118 MPa | 17100 psi | 2.8mm/min; ASTM D790 |
| Flexural Modulus | 3.04 GPa | 441 ksi | 2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
0.918 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 261 °C | 502 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 250 - 300 °C | 482 - 572 °F | Cylinder Temperature |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylex® P1332L Polycarbonate, UV Stabilized, Unreinforced
- LG Chemical XR404 ABS, Heat Resistance
- Borealis Casico™ FR4807 Non-Halogen Flame Retardant Compound for Low Voltage Insulation and Jacketing
- Hexcel® HexPly® M52 120°C/250°F Curing Epoxy, M52/40%/193P/CHS-3K
- Elisto THERMOSTAR® 4000 Mold Insulation Material
- 3M 2A05 Co-Extruded Polyethylene Protective Tapes
- Arlon 30580R025 0.025" (0.635 mm) Uncured Unsupported Silicone Rubber on Release Carrier
- Beijing Evergrow Resources ACFC1750 Activated Carbon Fiber Cloth
- Polykemi AB POLYfill PPC GF5020 PB Polypropylene Copolymer, Glass Fiber Reinforced, Chemically Coupled
- Beijing Evergrow Resources PTFE Sheet
Copyright © lookpolymers.com All Rights Reserved