SABIC Innovative Plastics LNP THERMOCOMP LX03447 PEEK
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP LX03447 PEEK.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* LX03447 is a compound based on Polyetheretherketone containing Proprietary Filler(s).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0700 % | 0.0700 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.030 cm/cm @Time 86400 sec |
0.0010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 246 MPa | 35700 psi | 5 mm/min; ISO 527 |
| 248 MPa | 36000 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 1.6 % | 1.6 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 28.35 GPa | 4112 ksi | 1 mm/min; ISO 527 |
| 28.54 GPa | 4139 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 360 MPa | 52200 psi | ISO 178 |
| 365 MPa | 52900 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 370 MPa | 53700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 23.7 GPa | 3440 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 23.8 GPa | 3450 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.700 J/cm | 1.31 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.71 J/cm | 14.4 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 9.00 µm/m-°C @Temperature -30.0 - 30.0 °C |
5.00 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 38.9 µm/m-°C @Temperature -30.0 - 30.0 °C |
21.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 335 °C | 635 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 337 °C @Thickness 3.20 mm |
639 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 318 °C | 604 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 325 °C @Thickness 3.20 mm |
617 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufGuard M™ GPP1001M-P-2986 Grey PP, Flame Retardant
- SABIC Innovative Plastics Lexan® LI1911R PC
- Overview of materials for Nylon 66, 30% Carbon Fiber Filled
- SABIC Innovative Plastics NORYL NH8006 PPE+HIPS (Europe-Africa-Middle East)
- Toyobo VYLOPET® EMC545 Injection Molding Polyester Resin, Glass Reinforced
- Polyram PlusTek RA303G7 Nylon 6.6, 35% Glass Fiber
- Dow INTEGRAL™ 936 High Heat Monolayer Adhesive Film
- Eurostar Starflam AFR560B1 PA66, Mineral/Glass Fiber Reinforced, Flame Retardant, Injection Molding
- ConocoPhillips 100 Ultra-Clean Super Hydraulic Oil
- RheTech Products GC15P200-01 15% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, Black
Copyright © lookpolymers.com All Rights Reserved