- Asia International Enterprise (Hong Kong) 6010FEN Nylon 66
Asia International Enterprise (Hong Kong) 6010FEN Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Asia Int'l Enterprise (Hong Kong) Limited |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asia International Enterprise (Hong Kong) 6010FEN Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asia International Enterprise (Hong Kong) Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc @Temperature 23.0 °C |
1.15 g/cc @Temperature 73.4 °F |
ASTM D792 |
| Filler Content | 0.00 % | 0.00 % | |
| Linear Mold Shrinkage | 0.0090 - 0.017 cm/cm | 0.0090 - 0.017 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Ultimate | 78.5 MPa | 11400 psi | 5mm/min; ASTM D638 |
| Elongation at Break | 30 % | 30 % | 5mm/min; ASTM D638 |
| Flexural Strength | 123 MPa | 17800 psi | 2.8mm/min; ASTM D790 |
| Flexural Modulus | 3.43 GPa | 498 ksi | 2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
0.918 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 261 °C | 502 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 250 - 300 °C | 482 - 572 °F | Cylinder Temperature |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 103 PC (Asia Pacific)
- SABIC Innovative Plastics LNP LUBRICOMP DCL32 PC (Europe-Africa-Middle East)
- Less Common Metals Gadolinium Vacuum Remelted Rare Earth Metal
- Lehmann & Voss LUVOCOM® 1-0784 Polyamide 66, with glass fiber and carbon fiber, heat stabilized
- Solvay Specialty Polymers Tecnoflon® FOR 9385F Fluoroelastomer
- Denka VINYKON W7100i PVC, W grade for non-migratory sheath and special items
- China Tungsten YT707 Tungsten Carbide
- 3M 7801 Aluminum Foil Label Material
- SABIC Innovative Plastics LNP LUBRICOMP CL001I PS
- Solvay RHODAFAC® MB Surfactant
Copyright © lookpolymers.com All Rights Reserved