Lehmann & Voss LUVOCOM® 1106-8133 Polyether imide, with carbon fiber, easy flowing
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1106-8133 Polyether imide, with carbon fiber, easy flowing.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: High-strength and high-stiff parts; low coefficient of expansion.High continuous use and heat distortion temperature. Non flammable.High dimensionally stable precision parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.Bearings, sleeves, control disks, gear wheels, pump impellers, gear parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | ISO 1183 |
| Water Absorption | <= 0.20 % | <= 0.20 % | 23°C/24h |
| Linear Mold Shrinkage | 0.00050 - 0.0030 cm/cm | 0.00050 - 0.0030 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 220 MPa | 31900 psi | |
| Elongation at Yield | 1.2 % | 1.2 % | |
| 1.5 % | 1.5 % | flexural | |
| Modulus of Elasticity | 21.0 GPa | 3050 ksi | |
| Flexural Strength | 315 MPa | 45700 psi | |
| Flexural Modulus | 18.0 GPa | 2610 ksi | |
| Charpy Impact Unnotched | 3.80 J/cm² | 18.1 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 170 °C | 338 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1e+05 | <= 1e+05 | |
| Insulation Resistance | <= 100000 ohm | <= 100000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 380 °C | 716 °F | mass temp |
| Nozzle Temperature | 350 - 400 °C | 662 - 752 °F | |
| Zone 1 | 330 - 350 °C | 626 - 662 °F | |
| Zone 2 | 340 - 390 °C | 644 - 734 °F | |
| Zone 3 | 350 - 400 °C | 662 - 752 °F | |
| Mold Temperature | 150 - 180 °C | 302 - 356 °F | |
| Drying Temperature | 120 °C @Time >=28800 sec |
248 °F @Time >=8.00 hour |
Dehumidifying dryer |
| 150 °C @Time >=14400 sec |
302 °F @Time >=4.00 hour |
or |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufTech™ GM-3968 PVC Compound
- LATI Latilub 57D-15T G/30 PPA, 30% Glass Fiber Reinforced
- Solvay RHODATERGE® BCC Surfactant
- A. Schulman POLYBATCH™ Green P30336 Concentrate Based In Homopolymer PP
- A. Schulman ComAlloy® E-16558 30% Glass Fiber Reinforced Nylon
- Master Bond UV15DC80 One Component, UV and Heat Curable Epoxy System
- Beijing Chemical Industry KAIFA® HN201-G20 PA6 Resin
- Austin Novel Materials Texalan® 665A Polyester and Polyether based TPU
- Haynes 556® alloy, sheet after 1000 hours at 871°C (1600°F)
- Ametek P316L P/M Stainless Steel, Sintered from 6.83 g/cc Green Density
Copyright © lookpolymers.com All Rights Reserved