Toyobo PELPRENE™ P80C Polyester TPE, High Flexibility, High Melting Point
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester TPE , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | Toyobo |
| Trade Name | Pelprene™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo PELPRENE™ P80C Polyester TPE, High Flexibility, High Melting Point.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Polyester TPE, High Flexibility, High Melting PointInformation provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.48 % | 0.48 % | 23°C, 65% RH |
| Linear Mold Shrinkage | 0.0060 cm/cm @Thickness 2.00 mm |
0.0060 in/in @Thickness 0.0787 in |
|
| Melt Index of Compound | 18 g/10 min @Temperature 230 °C |
18 g/10 min @Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 93 | 93 | JIS K6301 |
| Hardness, Shore D | 38 | 38 | ASTM D2240 |
| Tensile Strength at Break | 26.0 MPa | 3770 psi | ASTM D638 |
| Elongation at Break | 600 % | 600 % | ASTM D638 |
| 50% Modulus | 0.00640 GPa | 0.928 ksi | ASTM D638 |
| Flexural Modulus | 0.0490 GPa | 7.11 ksi | ASTM D790 |
| Compressive Modulus | 0.00420 GPa | 0.609 ksi | 0.1; ASTM D695 |
| Resilience | 78 | 78 | JIS K6301 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Tear Strength | 98.0 kN/m | 559 pli | ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 20 | 20 | ASTM D1044 |
| Compression Set | 49 % | 49 % | JIS K6301 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 170 µm/m-°C @Temperature 20.0 °C |
94.4 µin/in-°F @Temperature 68.0 °F |
TMA |
| Melting Point | 203 °C | 397 °F | By DSC |
| Maximum Service Temperature, Air | <= 25.0 °C | <= 77.0 °F | Heat deflection temperature, load unknown; ASTM D648 |
| Vicat Softening Point | 154 °C | 309 °F | ASTM D1525 |
| Brittleness Temperature | <= -65.0 °C | <= -85.0 °F | JIS K6301 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.20e+13 ohm-cm | 1.20e+13 ohm-cm | ASTM D257 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | JIS K2111 |
Users viewing this material also viewed the following:
- PolyOne Lubri-Tech™ SY-000/05T High Impact Styrene - 5% PTFE (discontinued **)
- Eastman Tenite 105-33 Cellulose Acetate (discontinued **)
- Kennametal Stellite Stellite® 706 Cobalt Alloy
- Gouda Vuurvast ADHESIET 160 Dry Air-Setting Refractory Mortar
- Silberline Sparkle Silver® 2750
- Zeon Chemicals Zealloy® 1453HM Modifier for Thermoplastics
- Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 25% Cold Reduction
- BASF Lucalen® A 3120 M Ethylene/Acrylate Copolymer
- Saint-Gobain Meldin® 1277 Thermoplastic Bearing Material
- Total Lacqrene® 4431 Flame Retardant Polystyrene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved