Ashley Polymers Ashlene® 190 Acetal
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | Ashley Polymers |
| Trade Name | Ashlene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ashley Polymers Ashlene® 190 Acetal.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A general purpose, medium viscosity, natural.Data provided by the manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 |
| Water Absorption | 0.22 % | 0.22 % | ASTM D570 |
| Linear Mold Shrinkage | 0.020 cm/cm | 0.020 in/in | ASTM D955 |
| Melt Flow | 9.0 g/10 min | 9.0 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 80 | 80 | ASTM D785 |
| Tensile Strength, Ultimate | 61.0 MPa | 8850 psi | ATSM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ASTM D790 |
| Shear Strength | 55.0 MPa | 7980 psi | ASTM D732 |
| Izod Impact, Notched | 0.640 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 158 °C | 316 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz |
3.7 @Frequency 1e+6 Hz |
ASTM D150 |
| Dissipation Factor | 0.0070 @Frequency 1e+6 Hz |
0.0070 @Frequency 1e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Parker Chomerics THERM-A-FORM T647 Cure-in-Place Potting and Underfill Material
- SABIC Innovative Plastics Lexan® XHT4143 PC Copolymer
- LNP Stat-Kon® PDX-E-99689 CCS Polyetherimide, Carbon Fiber Reinforcement (discontinued **)
- Menzolit Menzolit® BMC 0190 Unsaturated Polyester UP
- Sapco C 220 Steatite
- Zircar Zirconia Buster M-35 Alumina Board, Disc, and Cylinder Insulation
- EMS-Grivory Grivory® BGM-30 X PA6-(GF+MD)30
- Arlon 19220R025 0.025" (0.635 mm) Uncured Silicone Rubber with Fiberglass Substrate
- 3M Scotchkote™ SG 527 Epoxy Metal Repair
Copyright © lookpolymers.com All Rights Reserved