SABIC Innovative Plastics LNP Thermocomp RF007S PA 66 (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP THERMOCOMP
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP Thermocomp RF007S PA 66 (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* THERMOCOMP* RF007S is a compound based on PA 66 resin containing Glass Fiber . Added features include: Heat Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.

Physical Properties	Metric	English	Comments
Density	1.40 g/cc	0.0506 lb/inÂ³	ISO 1183
Linear Mold Shrinkage, Flow	0.0020 - 0.0050 cm/cm	0.0020 - 0.0050 in/in	SABIC Method

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	190 MPa	27600 psi	5 mm/min; ISO 527
Elongation at Break	3.0 %	3.0 %	5 mm/min; ISO 527
Flexural Yield Strength	265 MPa	38400 psi	2 mm/min; ISO 178
Flexural Modulus	9.00 GPa	1310 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	13.0 kJ/mÂ² @Temperature 23.0 Â°C	6.19 ft-lb/inÂ² @Temperature 73.4 Â°F	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	75.0 kJ/mÂ² @Temperature 23.0 Â°C	35.7 ft-lb/inÂ² @Temperature 73.4 Â°F	80104; ISO 180/1U

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	250 Â°C	482 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	UL 94