SABIC Innovative Plastics LNP LUBRICOMP DL0029E PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP DL0029E PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* DL0029E is a compound based on Polycarbonate resin containing 10% PTFE. Added features of this material include: Internally Lubricated, Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Density | 1.31 g/cc | 0.0473 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0100 % | 0.0100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Time 86400 sec |
0.0080 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 47.0 MPa | 6820 psi | Type I, 5 mm/min; ASTM D638 |
| 51.0 MPa | 7400 psi | ASTM D638 | |
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 26 % | 26 % | ASTM D638 |
| 33 % | 33 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 5.7 % | 5.7 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.24 GPa | 325 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 86.0 MPa | 12500 psi | ASTM D790 |
| Flexural Modulus | 2.33 GPa | 338 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.34 GPa | 339 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.19 J/cm | 2.23 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 20.2 J/cm | 37.8 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 46.0 J @Temperature 23.0 °C |
33.9 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.20 | 0.20 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.14 | 0.14 | ASTM D3702 Modified |
| K (wear) Factor | 111 x 10-8 mm³/N-M | 55.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 71.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
39.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 75.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
41.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C @Thickness 3.20 mm |
266 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.80 mm |
V-0 @Thickness 0.0709 in |
UL 94 |
Users viewing this material also viewed the following:
- Mitsui AURUM® JCN6230 Thermoplastic Polyimide Resin, Amorphous (discontinued **)
- Lehmann & Voss LUVOCOM® 1105-8356 PEEK, unreinforced
- Haynes 556® alloy, bar, after 8000 hours at 760°C (1400°F)
- SABIC Innovative Plastics LNP LUBRICOMP HFG25Z PA 11 (Asia Pacific)
- A. Schulman POLYBATCH™ U-7025-CFK Blowing Agent Concentrate Based In Polystyrene
- TIMCAL TIMREX® KS150-600SP Primary Synthetic Graphite
- Trimay® Wear Plate TWP61 Complex-carbide Flux Cored Weld Wire & Electrode
- Arkema Group Pebax® MV 1074 SN 01 Polyether Block Amide (PEBA) (Dry)
- Caplinq LINQSTAT™ VCF-40009.5S/2
- PolyOne Edgetek® UR-30GF/000 Natural Thermoplastic Polyurethane (Ether-Based), 30% Glass Fiber Reinforced (di
Copyright © lookpolymers.com All Rights Reserved