Asahi Kasei Tenac® FA405 Acetal Homopolymer, Low Friction Grade  (discontinued **)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Asahi Kasei Tenac® FA405 Acetal Homopolymer, Low Friction Grade  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Contains fluoropolymer and lubricant; excellent friction and wear on plastics.Applications: Bearings for printers, cams, gears.This product is not a part of the standard product line dated 2003.
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ASTM D792
Water Absorption 0.20 %
0.20 %
ASTM D570
Linear Mold Shrinkage 0.018 - 0.022 cm/cm
0.018 - 0.022 in/in
Asahi Chemical test
Melt Flow 9.0 g/10 min
9.0 g/10 min
melt index; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 94
94
ASTM D785
Tensile Strength, Ultimate 63.0 MPa
9140 psi
5 mm/min; parallel to flow; ASTM D638
Elongation at Break 35 %
35 %
5 mm/min; parallel to flow; ASTM D638
Flexural Yield Strength 98.0 MPa
14200 psi
ASTM D790
Flexural Modulus 2.90 GPa
421 ksi
ASTM D790
Izod Impact, Notched 0.590 J/cm
1.11 ft-lb/in
ASTM D256
Taber Abrasion, mg/1000 Cycles 10
10
ASTM D1044
Thermal Properties Metric English Comments
CTE, linear 100 µm/m-°C

@Temperature 20.0 °C
55.6 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 170 °C
338 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 136 °C
277 °F
ASTM D648
Flammability, UL94 HB
HB
Processing Properties Metric English Comments
Processing Temperature 190 - 210 °C
374 - 410 °F
Cylinder temp
Mold Temperature 60.0 - 120 °C
140 - 248 °F
Drying Temperature 89.0 - 90.0 °C
192 - 194 °F
Drying generally not required. If it is required, drying at 80-90°C for 3-4 hours will suffice.
Dry Time 3 - 4 hour
3 - 4 hour